牌号简介 About |
---|
TEKAMID™ H14HT是一种丙烯腈丁二烯苯乙烯 + 尼龙(ABS+尼龙)产品,。 它,在亚太地区有供货。 特性包括: 阻燃/额定火焰 High Toughness Features H14HT is a unreinforced PA/ABS with high impact strength, excellent processability. Application Automotive construction, sports and recreation, electrical/electronics Drying Product is dried and packed with a moisture content of <0.16%. Should the Packaging become damaged or be left open too long, then the material must be Dried. A too high moisture content can lead to a reduction of optical and Mechanical properties. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.07 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.70 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.90 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
断裂 fracture 2 |
51.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
100 | % | ASTM D638 |
弯曲模量 Bending modulus 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength 3 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃,3.2mm -30℃,3.2mm |
J/m | ASTM D256 | |
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 60°C Mold Temperature |
【新闻资讯】查看全部 ![]()
晶华引领深圳国际胶粘带、维护膜及光学膜展览会新风潮
2016-09-14 1928年美国人理查・德鲁发明了第一款胶带,经过一个多世纪的发展,胶带行业已经成为世界各国的重要基础化工子行业,是橡胶制品业的重要组成部分。随着新兴工业国家的崛起,世界胶带业的竞争重点在新世纪已经开始由传统的欧美工业国家向亚太新兴工业国家转移,形成了在亚太发展中国家间迅猛扩张的趋势,以中国为代表的亚太经济体已经成为世界胶带业的重要竞争力量,是世界胶带的主要生产国和消费国。 高性能薄膜制造技术展览会(简称:FILM EXPO )和胶粘带、保护膜及光学膜展览会(简称:APFO |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |