牌号简介 About |
---|
Softell CA 02 A是一种反应器TPO(热塑性聚烯烃),采用Lyondellbasell专有的Catalloy工艺技术制造。主要用于极软薄膜和片材的挤出、压延和挤出吹塑。Softell CA 02 A具有优异的低刚度、优异的低硬度和很好的抗冲击性。Softell CA 02 A显示了与填料、阻燃添加剂以及其他聚烯烃的高相容性。该等级为天然颗粒形式。 Softell CA 02 A is a reactor TPO (thermoplastic polyolefin) manufactured using the LyondellBasell's proprietary Catalloy process technology. It is primarily used for the extrusion, calendering and extrusion blow molding of very soft film and sheet. Softell CA 02 A exhibits outstanding low stiffness, excellent low hardness and very good impact resistance. Softell CA 02 A shows high compatibility to fillers and flame retardant additives as well as to other polyolefins. The grade is available in natural pellet form. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.870 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
0.60 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
75 | ISO 868 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
10.0 | MPa | ISO 527-2 |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
> 500 | % | ISO 527-2 |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
东丽新型PBT在不影响尺寸稳定性和可塑度的情况下减少了介电损耗
2021-07-14 搜料网资讯: 日本东丽工业公司开发了一种高性能PBT,其在高频毫米波段的介电损耗比传统PBT低40%,且不影响尺寸稳定性或可模塑性。东丽表示,这种材料将显著提高5G基站和自动驾驶 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |