牌号简介 About |
---|
Aegis® H8202NLB是一种未填充、低/中粘度、无润滑尼龙6注射成型均聚物,具有良好的填充薄片的熔融流动性。它具有良好的强度、刚度和韧性,以及优异的耐热性、化学性和耐磨性。 Aegis® H8202NLB is an unfilled, low/medium viscosity, non-lubricated nylon 6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It exhibits good strength, stiffness, and toughness as well as excellent heat, chemical and abrasion resistance. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.13 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
235℃,1.0kg 235℃,1.0kg |
9.8 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
1.3 | % | ASTM D955 |
吸水率 Water absorption rate |
ASTM D570 | ||
24hr 24hr |
1.6 | % | ASTM D570 |
饱和 saturated |
9.5 | % | ASTM D570 |
平衡 balance |
% | ASTM D570 | |
Extractables Extractables 2 |
% | 内部方法 | |
含水量 water content |
% | ASTM D6869 | |
相对粘度 Relative viscosity |
|||
@ 96% SAV @ 96% SAV |
|||
粘度 viscosity |
|||
FAV FAV |
ASTM D789 | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-40℃ -40℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
熔融温度 Melting temperature |
℃ | ASTM D3418 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM E831 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
屈服,23℃ Yield, 23 ℃ |
% | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Test Method: SOP-702-307 |
【新闻资讯】查看全部
耐300℃,三菱化学推出碳纤维增强酚醛树脂复合材料
2021-06-24 搜料网资讯: 近日,日本三菱化学株式会社宣布已开发出兼具轻质、刚性和高耐热性的碳纤维复合材料 (CFRP),以酚醛树脂为基体树脂,具有高耐热性,即使在300C下其物理性能也不会降 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |