牌号简介 About |
---|
EPO-TEK® H20E-LC是一种双组分、充银环氧树脂系统,专门设计用于微电子和光电应用中的芯片键合。由于其高导热性,它也被广泛用于热管理应用。经过多年的使用证明,它非常可靠,是低氯化物应用的导电粘合剂的首选。 EPO-TEK® H20E-LC is a two component, silver-filled epoxy system designed specifically for chip bonding in microelectronic and optoelectronic applications. It is also used extensively for thermal management applications due to its high thermal conductivity. It has proven itself to be extremely reliable over many years of service and is the conductive adhesive of choice for low chloride applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颗粒大小 Particle size |
< 45.0 | µm | |
离子类型 Ionic type |
|||
Cl- Cl- |
11 | ppm | |
K+ K+ |
2 | ppm | |
Na+ Na+ |
6 | ppm | |
NH4+ NH4+ |
259 | ppm | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Degradation Temperature Degradation Temperature |
℃ | ||
Die Shear Strength(>5 kg,23℃) Die Shear Strength(>5 kg,23℃) |
MPa | ||
工作温度 working temperature |
|||
Continuous Continuous |
℃ | ||
Intermittent Intermittent |
℃ | ||
Storage Modulus Storage Modulus |
GPa | ||
触变指数 Thixotropic index |
|||
加热减量 Heating reduction |
|||
200℃ 200℃ |
% | ||
250℃ 250℃ |
% | ||
300℃ 300℃ |
% | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颜色 colour |
|||
-- -- 5 |
|||
密度 Density |
|||
Part A Part A |
g/cm³ | ||
Part B Part B |
g/cm³ | ||
粘度 viscosity 7 |
|||
23℃ 23℃ 7 |
Pa·s | ||
固化时间 Curing time |
|||
150℃ 150℃ |
hr | ||
储存稳定性 storage stability |
min | ||
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
|||
搭接剪切强度 lap shear strength |
|||
23℃ 23℃ |
MPa | ||
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature 2 |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
|||
-- -- 3 |
cm/cm/℃ | ||
-- -- 4 |
cm/cm/℃ | ||
导热系数 Thermal conductivity coefficient |
W/m/K | ||
热固组件 Thermosetting components |
|||
部件 A Component A |
|||
部件 B Component B |
|||
贮藏期限 Storage period |
|||
23℃ 23℃ |
wk |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
3 Below Tg |
4 Above Tg |
5 Part B |
6 Part A |
7 100 rpm |
【新闻资讯】查看全部
我国将大力推进“新塑料经济”开展
2016-11-10 11月3日,为推动废塑料产业变革与创新,构建产业新生态,第十六届中国塑料回收和再生大会在厦门召开。工业和信息化部节能与综合利用司、环境保护部固废中心、海关总署监管司、中国合成树脂供销协会塑料循环利用分会、中国废塑料协会以及来自全国31个省市自治区和港澳台、欧美、日本等10个国家和地区的产业界代表500余人参加了会议。 工业和信息化部节能与综合利用司代表在会上强调,再生资源产业发展已成为绿色环保产业的重要组成部分,是推动绿色增长的新动能,大力推动再生资源产业发展对于促进供给侧 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |