Sarlink ML-1690B BLK是一款通用型TPE,专为汽车内饰设计。这是一个高硬度,中等密度等级适合注塑成型。这种高流量热塑性弹性体显示出改善的可塑性和表面外观。 Sarlink ML-1690B BLK is a general purpose TPE designed for automotive interior applications. This is a high hardness, medium density grade suitable for injection molding. This high flow TPE exhibits improved moldability and surface appearance. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,1 秒,注塑成型 Shore A, 1 second, injection molding |
92 | ||
邵氏 A,5 秒,注塑成型 Shore A, 5 seconds, injection molding |
91 | ||
邵氏 A,15 秒,注塑成型 Shore A, 15 seconds, injection molding |
90 | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
TD,断裂 TD, fracture |
MPa | ||
MD,断裂 MD, fracture |
MPa | ||
拉伸应变 Tensile strain 2 |
|||
TD,断裂 TD, fracture |
% | ||
流量,断裂 Flow rate, fracture |
% | ||
撕裂强度 tear strength 3 |
|||
TD TD |
kN/m | ||
MD MD |
kN/m | ||
压缩形变 Compression deformation 4 |
|||
23℃,22 hr 23℃,22 hr |
% | ||
70℃,22 hr 70℃,22 hr |
% | ||
90℃,70 hr 90℃,70 hr |
% | ||
125℃,70 hr 125℃,70 hr |
% | ||
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air 5 |
|||
TD:110℃,1008 hr TD:110℃,1008 hr |
% | ||
MD:110℃,1008 hr MD:110℃,1008 hr |
% | ||
TD:100% 应变 110℃,1008 hr TD: 100% strain at 110 ℃, 1008 hr |
% | ||
MD:100% 应变 110℃,1008 hr MD: 100% strain at 110 ℃, 1008 hr |
% | ||
TD:125℃,168 hr TD:125℃,168 hr |
% | ||
MD:125℃,168 hr MD:125℃,168 hr |
% | ||
TD:100% 应变 125℃,168 hr TD: 100% strain 125 ℃, 168 hr |
% | ||
MD:100% 应变 125℃,168 hr MD: 100% strain 125 ℃, 168 hr |
% | ||
在空气中断裂时拉伸应力变化 Changes in tensile stress during fracture in air 5 |
|||
TD:110℃,1008 hr TD:110℃,1008 hr |
% | ||
流量:110℃,1008 hr Flow rate: 110 ℃, 1008 hr |
% | ||
TD:125℃,168 hr TD:125℃,168 hr |
% | ||
流量:125℃,168 hr Flow rate: 125 ℃, 168 hr |
% | ||
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
|||
邵氏 A,110℃,1008 hr Shore A, 110 ℃, 1008 hr 6 |
|||
邵氏 A,110℃,1008 hr Shore A, 110 ℃, 1008 hr 7 |
|||
邵氏 A,110℃,1008 hr Shore A, 110 ℃, 1008 hr 8 |
|||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr 6 |
|||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr 7 |
|||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr 8 |
|||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
氙老化测试机 Xenon aging testing machine |
|||
Delta E - 1250 kJ Delta E - 1250 kJ |
|||
Delta E - 2500 kJ Delta E - 2500 kJ |
|||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
g/10min | ASTM D1238 | |
熔体表观粘度 Apparent viscosity of melt |
|||
200℃,206 sec^-1 200℃,206 sec^-1 |
Pa·s | ASTM D3835 | |
特殊值 |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
TD,100% 应变 TD, 100% strain |
4.90 | MPa | |
MD,100% 应变 MD, 100% strain |
6.17 | MPa |
备注 |
---|
2、类型 1, 510 mm/min |
3、B 方法,直角形试样(不割口), 510 mm/min |
4、类型 A |
5、类型 1 |
6、15 sec |
7、5 sec |
8、1 sec |
【新闻资讯】查看全部
松下推出新型密封及粘合资料 用于车载开关及传感器
2016-02-17 松下汽车电子和机电系统公司(Panasonic Automotive & Industrial Systems Company)将从2016年3月开始量产用于密封及粘合加工用途的材料“激光熔敷用聚对苯二甲酸丁二醇酯(PBT)树脂成型材料”。据介绍,使用该材料可减少车载设备用开关及传感器等的生产工序、提高长期可靠性及设计自由度。 为了使该材料产品化,该公司开发出了“合金化技术”,利用该技术可高效率透过、吸收激光,瞬间熔融,使海岛构造(含有多种成分的高分子相态的一种)均 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名:搜料网-Sarlink® TPE ML-1690B BLK (PRELIMINARY DATA)证书
发送至:(多个地址,中间以逗号隔开)
发送一份副本给我:您还没有填写邮箱!(点击完善资料)