牌号简介 About |
---|
甲烯烃E924是一种双模高密度聚乙烯(HMW-HDPE)树脂,具有高的抗冲击强度和良好的加工性能。该树脂在整体物理性能上具有良好的平衡性,并为薄膜应用提供良好的刚度。甲烯烃E924符合21 CFR 177.1520中规定的美国食品药品监督管理局的所有要求,包括用于食品直接接触的聚烯烃制品的安全使用。 Formolene E924 is a bimodal HMW-HDPE resin designed for high dart impact strength and good processing characteristics. The resin is well balanced in overall physical properties and provides good stiffness for thin gauge film applications. Formolene E924 meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.949 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,2.16kg 190℃,2.16kg 2 |
0.040 | g/10min | ASTM D1238 |
190℃,21.6kg 190℃,21.6kg 3 |
8.5 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
13 | µm | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂,13 µm MD, fracture, 13 µ m |
62.1 | MPa | ASTM D882 |
TD,断裂,13 µm TD, fracture, 13 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,13 µm MD, fracture, 13 µ m |
% | ASTM D882 | |
TD,断裂,13 µm TD, fracture, 13 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
13 µm 13 µm |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:13 µm MD:13 µm |
g | ASTM D1922 | |
TD:13 µm TD:13 µm |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
℃ | DSC |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 MI |
3 HLMI |
【新闻资讯】查看全部
浅谈塑料机械行业的数字化展开新契机
2018-05-30 对于塑料机械行业而言,数字化发展既为其带来了新的商机,又是其迎接未来挑战的必经之路。数字化发展不仅体现在生产流程方面,更表现在企业管理、用户体验方面。作为走在技术前沿的塑料机械行业,面对新的机遇与挑战,应在不断的突变中寻求适合自己的发展道路。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |