牌号简介 About |
---|
EMAC树脂能粘附并与各种材料相容,包括纸张、聚烯烃、定向聚烯烃、聚酯、离聚物、聚偏二氯乙烯、未增塑聚氯乙烯和其他极性聚合物。用作热封层、粘合层或用于提高成本/性能的改性剂。在环境温度和冷冻温度下,它们柔软、柔韧、坚韧,并具有良好的抗静电性能。这些聚合物具有高固体填充性和与多种聚合物的相容性。这有助于将其用作各种用途的浓缩物的碱,以添加到广泛的聚合物中。EMAC树脂工艺,如LDPE。EMAC+特种共聚物采用专利技术生产:美国专利5804675。 EMAC resins adhere to and are compatible with a wide range of materials including paper, polyolefins, oriented polyolefins, polyesters, ionomers, PVdC, unplasticized PVC and other polar polymers. For use as heat seal layer, adhesive layer, or modifier for cost/performance enhancement. They are soft, pliable and tough at ambient and freezing temperatures and exhibit excellent ESCR. These polymers exhibit high solids fillability and compatibility with a wide range of polymers. This facilitates their uses as bases for all-purpose concentrates for addition to a wide spectrum of polymers. EMAC resins process like LDPE. EMAC+ Specialty Copolymers are produced under patented technology: US Patent 5804675. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.940 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.4 | g/10min | ASTM D1238 |
甲基丙烯酸含量 Methacrylic acid content |
21.5 | wt% | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
32 | ASTM D2240 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
|||
1% 正割,TD 1% secant, TD |
28.0 | MPa | ASTM D882 |
1% 正割,MD 1% secant, MD |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
|||
断裂 fracture 2 |
MPa | ASTM D638 | |
TD,断裂 TD, fracture |
MPa | ASTM D882 | |
MD,断裂 MD, fracture |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 2 |
% | ASTM D638 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
MD,断裂 MD, fracture |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD MD |
g | ASTM D1922 | |
撕裂强度 tear strength |
|||
TD TD |
g | ASTM D1922 | |
始封温度 Initial sealing temperature |
℃ | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45° 45° |
ASTM D2457 | ||
雾度 Haze |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 4, 20 in/min |
【新闻资讯】查看全部
巴斯夫正在扩展德国固化丙烯酸酯的生产才能
2016-06-14 巴斯夫正在扩大其现有位于德国路德维希港的生产设施的Laromer®UV/EB固化丙烯酸酯的生产能力,该设施是巴斯夫的C3一体化系统的一部分。通过提高该产品的生产能力,巴斯夫可以满足市场对高品质的UV/EB丙烯酸酯需求上升,并加强作为一个世界领先的UV固化涂料和油墨连接料树脂制造商的地位。新增产能将在2016年第三季度供应市场。 UV/EB固化树脂作为巴斯夫业务增长的支柱之一,早在2014年,巴斯夫为了满足市场增长的需求,在法国Meaux新建了生产设施。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |