牌号简介 About |
---|
XT聚合物X800RG化合物是一种冲击改性丙烯酸基多聚物,用于成型和挤出应用。XT聚合物丙烯酸基多聚物化合物的典型性能有:优异的热成型性、优越的热变形温度、优异的粘合和焊接性能、良好的冲击强度、良好的透光性、耐ETO、γ和电子束杀菌性、耐PVC稳定剂。XT聚合物X80的特殊性能0RG化合物有:高熔体流动速率,良好的耐化学性应用:用于食品包装和电器配件。 XT polymer X800RG compound is an impact-modified acrylic-based multipolymer for molding and extrusion applications. Typical properties of XT® polymer acrylic-based multipolymer compounds are: outstanding thermoformability superior heat distortion temperatures excellent bonding and welding capabilities good impact strength good light transmission resistant to EtO, gamma and E-beam sterilization resistant to PVC stabilizers The special properties of XT polymer X800RG compound are: high melt flow rate good chemical resistance Application: Used for food packaging and appliance parts. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.11 | g/cm³ | ASTM D792 |
表观密度 Apparent density |
0.65 | g/cm³ | ASTM D1895 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,5.0kg 230℃,5.0kg |
11 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.40 to 0.70 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
平衡 balance |
< 0.30 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
0℃,6.4mm 0℃,6.4mm |
J/m | ASTM D256 | |
23℃,6.4mm 23℃,6.4mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火,6.35 mm 1.8 MPa, annealed, 6.35 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:0~100℃ MD:0~100℃ |
1/℃ | ASTM D696 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透光率 Transmittance |
|||
3200 µm 3200 µm |
% | ASTM D1003 | |
雾度 Haze |
|||
3200 µm 3200 µm |
% | ASTM D1003 | |
黄度指数 Yellowness index |
|||
3.20 mm 3.20 mm |
YI | Internal Method | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
Stratasys子公司推出新的高速塑料3D打印
2017-09-27 《3D打印世界》讯/Stratasys全资子公司Evolve Additive Solutions推出新的高速塑料3D打印工艺。据称,自2009年以来,所谓的基于电子照相的增材制造工艺(EPSD)已经发展到比“下一代最快的AM塑料技术还要快50倍”。 Evolve Additive的技术以1938年发明的大多数复印机和激光打印机的专有技术为基础。在2D打印中,电子照相术(也称为静电复印)使用静电荷将图像附着到基底(即纸)上。2D电子照相术中的纸本质上代表3D印刷物体的单层。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |