牌号简介 About |
---|
亲和力*PL 1880G聚烯烃塑性体(POP)是通过InSite*技术生产的。它是一种乙烯-α-烯烃树脂,设计用于各种苛刻的包装应用,包括高速,表格填充密封包装。这种树脂提供卓越的最终热粘强度和低温密封启动,即使通过污染的包装。低密封起始温度优良的热粘强度高性能密封层在软包装中符合:美国FDA FCN 424 U.S.FDA-DMF U.S.USP 23 HPFB无异议(有限制)欧盟,2011年10月10日日本卫生烯烃和苯乙烯塑料协会咨询法规的完整细节。 AFFINITY* PL 1880G Polyolefin Plastomer (POP) is produced via INSITE* Technology. It is an ethylene alpha-olefin resin designed for use in a variety of demanding packaging applications, including high-speed, form-fill-seal packaging. This resin offers excellent ultimate hot tack strength and low temperature seal initiation, even through contamination in the package. Low seal initiation temperature Excellent hot tack strength High performance sealant layer in flexible packaging Complies with: U.S. FDA FCN 424 U.S. FDA-DMF U.S. USP 23 HPFB No Objection (with limitations) EU, No 10/2011 Japan Hygienic Olefin and Styrene lastics Association Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.902 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
51 | µm | |
膜刺穿强度 Membrane puncture strength |
|||
51 µm 51 µm |
8.81 | J | 内部方法 |
膜刺穿力 Membrane puncture force |
|||
51 µm 51 µm |
92.5 | N | 内部方法 |
膜耐刺穿性 Membrane puncture resistance |
|||
51 µm 51 µm |
J/cm³ | 内部方法 | |
割线模量 Secant modulus |
ASTM D882 | ||
2% 正割,MD:51 µm 2% secant, MD: 51 µ m |
MPa | ASTM D882 | |
2% 正割,TD:51 µm 2% secant, TD: 51 µ m |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,51 µm MD, yield, 51 µ m |
MPa | ASTM D882 | |
TD,屈服,51 µm TD, yield, 51 µ m |
MPa | ASTM D882 | |
MD,断裂,51 µm MD, fracture, 51 µ m |
MPa | ASTM D882 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,51 µm MD, fracture, 51 µ m |
% | ASTM D882 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
51 µm 51 µm |
g | ASTM D1709-B | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 2 |
ASTM D1922 | ||
MD:51 µm MD:51 µm |
g | ASTM D1922 | |
TD:51 µm TD:51 µm |
g | ASTM D1922 | |
始封温度 Initial sealing temperature 3 |
|||
51 µm 51 µm 3 |
℃ | 内部方法 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
20°,50.8 µm 20°,50.8 µm |
ASTM D2457 | ||
透明度 transparency |
|||
50.8 µm 50.8 µm |
ASTM D1746 | ||
雾度 Haze |
|||
50.8 µm 50.8 µm |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 改性过的矩形测件。 |
3 实现 2 磅/英寸 (8.8 N/25.4 mm) 热封强度的温度。 热封强度,Topwave HT 测试仪 0.5 S 保压,40 psi 压力,拉动速度 10 英寸/分(250 mm/秒)。 |
【新闻资讯】查看全部 ![]()
莫斯科举行Interplastica展会
2018-12-20 2019年1月29至2月1日,在莫斯科举行的Interplastica展会中,威猛巴顿菲尔将在2.1/A23展位,展示其最新的注塑成型技术及自动化和辅助设备。 在2019 Interplastica展会中,威猛巴顿菲尔将展示其配备了最新威猛模内贴标(IML)单元的新的EcoPower Xpress 160/1100+注塑机。 EcoPower Xpress是一款全电动、高速和高性能的注塑机,专为包装行业所需的高产量薄壁应用而 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |