牌号简介 About |
---|
IROGRAN® A 95 E 4861是一种高性能聚酯基热塑性聚氨酯,用于挤压应用。IROGRAN® A 95 E 4861是亨斯迈技术挤压产品系列的一部分,提供一种特殊设计的柔性材料,具有宽的加工窗口,特别适用于制备挤压薄膜。性能特点:耐水解性好,结晶率高,低温柔韧性好,加工性好。 IROGRAN A 95 E 4861 is a high performance polyester based thermoplastic polyurethane intended for extrusion applications. IROGRAN A 95 E 4861 is part of the HUNTSMAN technical extrusion product range and offers a specially designed, flexible material with a broad processing window particularly suitable for the preparation of extruded films. PERFORMANCE FEATURES Excellent hydrolysis resistance High crystallization rate Good low temperature flexibility Good processability |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
1.22 | g/cm³ | ASTM D792 |
密度 Density 3 |
1.22 | g/cm³ | DIN 53479 |
熔体质量流动速率 Melt Flow Rate |
|||
215℃,21.6kg 215℃,21.6kg |
45 | g/10min | |
收缩率 Shrinkage rate |
|||
MD:注塑成型 MD: Injection molding |
1.1 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A,注塑成型 Shaw A, injection molding |
98 | ASTM D2240 | |
邵氏 D,注塑成型 Shaw's D, injection molding |
ASTM D2240 | ||
邵氏硬度 Shore hardness |
DIN 53505 | ||
邵氏 A,注塑成型 Shaw A, injection molding |
DIN 53505 | ||
邵氏 D,注塑成型 Shaw's D, injection molding |
DIN 53505 | ||
磨耗量 Wear amount 2 |
|||
-- -- |
mm³ | DIN 53516 | |
-- -- |
mm³ | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
断裂 fracture 2 |
MPa | ASTM D412 | |
断裂 fracture 2 |
MPa | DIN 53504 | |
300% 应变 300% strain 2 |
MPa | ASTM D412 | |
300% 应变 300% strain 2 |
MPa | DIN 53504 | |
100% 应变 100% strain 2 |
MPa | ASTM D412 | |
100% 应变 100% strain 2 |
MPa | DIN 53504 | |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
% | ASTM D412 | |
断裂 fracture 2 |
% | DIN 53504 | |
撕裂强度 tear strength 2 |
kN/m | ASTM D624 | |
撕裂强度 tear strength 2 |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation 2 |
ASTM D395 | ||
23℃,70 hr 23℃,70 hr |
% | ASTM D395 | |
70℃,24 hr 70℃,24 hr |
% | ASTM D395 | |
压缩形变 Compression deformation 2 |
ISO 815 | ||
23℃,70 hr 23℃,70 hr |
% | ISO 815 | |
70℃,24 hr 70℃,24 hr |
% | ISO 815 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Injection Molded |
【新闻资讯】查看全部
ForTii®Ace MX53T 推翻汽车零件开发流程
2018-11-28 以塑代钢为汽车制造业带来的红利可谓不胜枚举:整车减重,更大的设计自由度,零部件集成化,系统成本降低,降噪减震,提高对各种矿物油、燃料、除雪剂、冷却剂、蓄电池电解液 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |