牌号简介 About |
---|
说明:PB208是一种不含添加剂的低密度聚乙烯。该等级显示出良好的加工性能,适用于低粘度要求的应用。该树脂的注塑制品具有良好的流动性和柔韧性。添加剂:目前没有添加剂的应用:母粒;大面积的盖子和注射件。工艺:注射成型 PB208 is a low density polyethylene with no additives. This grade shows excellent processability being indicated for low viscosity required applications. Injection molded products with this resin shows good flow and flexibility properties. Additive: No additives present Applications: Masterbatches; Covers and injected parts with large flat area. Process: Injection Molding |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.923 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
22 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,模压成型 Shaw's D, molded |
45 | ASTM D2240 | |
拉伸强度 tensile strength |
|||
断裂,模压成型 Fracture, molded |
8.00 | MPa | ASTM D638 |
屈服,模压成型 Yield, molding |
10.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂,模压成型 Fracture, molded |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
1% 正割,模压成型 1% cut, molded |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 压 力1 (10N) |
【新闻资讯】查看全部
玻纤增强资料的优缺陷有哪些?
2018-02-06 玻纤增强塑料是在原有纯塑料的基础上,加入玻璃纤维和其它助剂,从而提高材料的使用范围。 一般的来说,大部分的玻纤增强材料多用在产品的结构零件上,是一种结构工程材料;如:PP ABS PA66 PA6 PC POM PPO PET PBT PPS 优点: 1.玻纤增强以后,玻纤是耐高温材料,因此,增强塑料的耐热温度比不加玻纤以前提高很多,尤其是尼龙类塑料; 2.玻纤增强以后,由于玻纤的加入,限制了 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |