牌号简介 About |
---|
Vibrathane B895是一种MDI端接的聚醚基预聚物。预聚物是室温下的液体。Vibrathane B895在1,4丁二醇和95邵尔A的重量比为80/20的HQEE/1,4 bd的条件下固化时,生成90邵尔硬度的聚氨酯。Vibrathane B895在加工温度下粘度低,工作寿命适用于机器和手工配料程序。该产品的典型应用包括溜冰轮。 VIBRATHANE B895 is an MDI-terminated, polyether based prepolymer. The prepolymer is a liquid at room temperature. VIBRATHANE B895 yields a 90 Shore hardness urethane when cured with 1,4 Butanediol and a 95 Shore A when cured with an 80/20 weight ratio of HQEE/1,4 BD. VIBRATHANE B895, at processing temperature, is low in viscosity and has a working life suitable for both machine and hand-batching procedures. Typical applications for this product include skate wheels. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
95 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
100% 应变 100% strain |
10.3 | MPa | ASTM D412 |
200% 应变 200% strain |
11.7 | MPa | ASTM D412 |
300% 应变 300% strain |
13.1 | MPa | ASTM D412 |
拉伸强度 tensile strength |
16.9 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength |
|||
-- -- 2 |
kN/m | ASTM D624 | |
开裂 cracking |
kN/m | ASTM D470 | |
压缩形变 Compression deformation |
|||
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
储存稳定性 storage stability |
min | ||
脱模时间 stripping time |
min | ||
后固化时间 Post curing time |
|||
115℃ 115℃ |
hr |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
【新闻资讯】查看全部
索尔维扩建上海研发中心 聚焦高功能材料应用研讨
2019-11-22 中国在全球化工市场中的地位越来越重要,今年3月刚上任的索尔维首席执行官兼执行委员会主席Ilham Kadri接受第一财经记者采访时表示:未来十年,我们希望索尔维的中国市场销售额至 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |