牌号简介 About |
---|
flexathene pd 907是一种热塑性烯烃(TPO),用于挤出和热成型应用。pd 907具有优异的耐低温冲击性和刚度平衡。pd 907是专门为高熔融强度,良好的尺寸稳定性和与油漆膜层压使用而设计的。本产品易于再加工,加工特性或物理性质变化最小。 FLEXATHENE PD 907 is a thermoplastic olefin (TPO) formulated for extrusion and thermoforming applications. PD 907 has an excellent balance of cold temperature impact resistance and stiffness. PD 907 is specially formulated for high melt strength, excellent dimensional stability and for use with paint film lamination. This product is readily reprocessed with minimal changes to processing characteristics or physical properties. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- |
0.967 | g/cm³ | ISO 1183/A |
-- -- |
0.976 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
2.1 | g/10min | ASTM D1238 |
230℃,2.16kg 230℃,2.16kg 2 |
2.1 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
0.89 到 1.2 | % | ISO 294-4 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
正割 Secant |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
正切 tangent 3 |
MPa | ASTM D790-B | |
正割 Secant |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
-18℃ -18℃ |
ASTM D256 | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-30℃ -30℃ |
ASTM D4812 | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 4 |
ASTM D3763 | ||
-30℃,Energy to Peak Load,韧性破坏 -30 ℃, Energy to Peak Load, toughness failure |
J | ASTM D3763 | |
23℃,Energy to Peak Load,韧性破坏 23 ℃, Energy to Peak Load, toughness failure |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM E831 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 程序 A |
3 0.050 in/min |
4 7.22 ft/sec |
【新闻资讯】查看全部
PET工程塑料开展史 涨姿态!
2017-08-09 聚对苯二甲酸乙二酯(PET)是一种性能优良的热塑性塑料,其熔融温度和玻璃化转变温度较高,具有良好的耐热性、抗蠕变性、耐疲劳性、耐摩擦与磨损性、电绝缘性及耐化学药品性,被广泛用于合成纤维、薄膜、工程塑料、医药和日用品等领域。PET价格低廉,20世纪60年代便开始了作为工程塑料的应用开发,目前已应用于汽车、电机、电子、家用电器及机械等行业。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |