牌号简介 About |
---|
MXSTEN® CV77523是一种专为吹塑薄膜挤出而设计的聚乙烯塑性体,它含有高滑动性、高抗阻塞性和聚合物加工助剂。用该树脂制备的薄膜具有很好的强度特性和较低的密封起始温度。应用/用途:农用管材吹塑薄膜食品包装 MXSTEN® CV77523 is a polyethylene plastomer designed for blown film extrusion that contains high slip, very high antiblock and polymer processing aid additives. Films produced with this resin exhibit very good strength properties, and low seal initiation temperatures. Application/Uses: Agricultural tubing Blown film Food packaging |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.906 | g/cm³ | ASTM D4883 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.50 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
割线模量 Secant modulus 2 |
|||
1% 正割,TD,25 µm,吹塑薄膜 1% secant, TD, 25 µ m, blow molded film 2 |
145 | MPa | ASTM D882 |
1% 正割,MD,25 µm,吹塑薄膜 1% secant, MD, 25 µ m, blow molded film 2 |
124 | MPa | ASTM D882 |
拉伸强度 tensile strength 2 |
|||
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film 2 |
MPa | ASTM D882 | |
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film 2 |
MPa | ASTM D882 | |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film 2 |
MPa | ASTM D882 | |
拉伸应变 Tensile strain 2 |
|||
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film 2 |
% | ASTM D882 | |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film 2 |
% | ASTM D882 | |
落锤冲击 Drop hammer impact 2 |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film 2 |
g | ASTM D1709 | |
撕裂强度 tear strength 2 |
|||
TD,25 µm,吹塑薄膜 TD, 25 µ m, blow molded film 2 |
g | ASTM D1922 | |
MD,25 µm,吹塑薄膜 MD, 25 µ m, blow molded film 2 |
g | ASTM D1922 | |
始封温度 Initial sealing temperature 3 |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film 3 |
℃ | Internal Method | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,25.4 µm,吹塑薄膜 45 °, 25.4 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
25.4 µm,吹塑薄膜 25.4 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Test run at 23°C (73°F) and 50% relative humidity |
3 Seal initiation temperature is the temperature at which 200 g/inch seal strength is achieved. |
【新闻资讯】查看全部
进口再生塑料颗粒被海关扣押 企业应留意哪些成绩?
2017-12-08 废料禁止进口,国内严查环保,随之而来的就是涨价潮、缺货潮。对于再生塑料下游行业,原料要从哪里来?路径该如何走?成为目前最大的难题。 1、进口再生颗粒按一般原料监管 在政策完成过程中,虽然对废旧塑料有了禁令,但是对塑料再生颗粒这方面,没有明显限制,对进口颗粒是重大利好,众多塑胶企业转向越南、泰国、马来西亚等国家进口再生颗粒。 2014年5月27日,中国废塑料协会提出“三个统一”监管方式,使大部分塑料再生颗粒按照 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |