牌号简介 About |
---|
主要特点UmaPET SI是透明膜,一面经过防静电处理。抗静电表面确保清洁和良好的处理特性。在软包装中的应用,作为层压板外表面的基材,有助于顺利地进行袋装等操作。电子设备及其零部件包装、集成电路板、印刷电路板、通信设备等工业应用。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
收缩率 Shrinkage rate |
ASTM D1204 | ||
MD:150℃,0.01 mm,30 min MD:150℃,0.01 mm,30 min |
2.5 | % | |
MD:150℃,0.012 mm,30 min MD:150℃,0.012 mm,30 min |
2.5 | % | |
MD:150℃,0.015 mm,30 min MD:150℃,0.015 mm,30 min |
2.5 | % | |
MD:150℃,0.023 mm,30 min MD:150℃,0.023 mm,30 min |
2.5 | % | |
TD:150℃,0.01 mm,30 min TD:150℃,0.01 mm,30 min |
0.40 | % | |
TD:150℃,0.012 mm,30 min TD:150℃,0.012 mm,30 min |
% | ||
TD:150℃,0.015 mm,30 min TD:150℃,0.015 mm,30 min |
% | ||
TD:150℃,0.023 mm,30 min TD:150℃,0.023 mm,30 min |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
ASTM D1894 | ||
与自身 - 动态 With oneself - dynamic 1 |
|||
与自身 - 动态 With oneself - dynamic 2 |
|||
与自身 - 动态 With oneself - dynamic 3 |
|||
与自身 - 动态 With oneself - dynamic 4 |
|||
与自身 - 静态 With oneself - static 5 |
|||
与自身 - 静态 With oneself - static 6 |
|||
与自身 - 静态 With oneself - static 7 |
|||
与自身 - 静态 With oneself - static 8 |
|||
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
µm | ||
薄膜厚度 film thickness |
|||
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂,10 µm MD, fracture, 10 µ m |
MPa | ||
MD,断裂,12 µm MD, fracture, 12 µ m |
MPa | ||
MD,断裂,15 µm MD, fracture, 15 µ m |
MPa | ||
MD,断裂,23 µm MD, fracture, 23 µ m |
MPa | ||
TD,断裂,10 µm TD, fracture, 10 µ m |
MPa | ||
TD,断裂,12 µm TD, fracture, 12 µ m |
MPa | ||
TD,断裂,15 µm TD, fracture, 15 µ m |
MPa | ||
TD,断裂,23 µm TD, fracture, 23 µ m |
MPa | ||
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,10 µm MD, fracture, 10 µ m |
% | ||
MD,断裂,12 µm MD, fracture, 12 µ m |
% | ||
MD,断裂,15 µm MD, fracture, 15 µ m |
% | ||
MD,断裂,23 µm MD, fracture, 23 µ m |
% | ||
TD,断裂,10 µm TD, fracture, 10 µ m |
% | ||
TD,断裂,12 µm TD, fracture, 12 µ m |
% | ||
TD,断裂,15 µm TD, fracture, 15 µ m |
% | ||
TD,断裂,23 µm TD, fracture, 23 µ m |
% | ||
用量 dosage |
内部方法 | ||
10.0 µm 10.0 µm |
m²/kg | ||
12.0 µm 12.0 µm |
m²/kg | ||
15.0 µm 15.0 µm |
m²/kg | ||
23.0 µm 23.0 µm |
m²/kg | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze |
ASTM D1003 | ||
10 µm 10 µm |
% | ||
12 µm 12 µm |
% | ||
15 µm 15 µm |
% | ||
23 µm 23 µm |
% | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Ash Pick Up Test Ash Pick Up Test |
内部方法 | ||
10.0 µm 10.0 µm |
|||
12.0 µm 12.0 µm |
|||
15.0 µm 15.0 µm |
|||
23.0 µm 23.0 µm |
|||
Surface Static Charge Surface Static Charge 9 |
内部方法 | ||
10.0 µm 10.0 µm |
|||
12.0 µm 12.0 µm |
|||
15.0 µm 15.0 µm |
|||
23.0 µm 23.0 µm |
|||
Wetting Tension - Plain side Wetting Tension - Plain side |
ASTM D2578 | ||
10.0 µm 10.0 µm |
dyne/cm | ||
12.0 µm 12.0 µm |
dyne/cm | ||
15.0 µm 15.0 µm |
dyne/cm | ||
23.0 µm 23.0 µm |
dyne/cm |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 12 µm |
3 10 µm |
4 15 µm |
5 23 µm |
6 Hand held static locator |
【新闻资讯】查看全部
50亿!茂名石化炼油转型升级项目正式获批!
2021-08-10 搜料网资讯: 2021年8月6日,茂名市生态环境局在官网公布了《中国石油化工股份有限公司茂名分公司炼油转型升级项目》获批文件! 7月28日,茂名市生态环境局进行了拟批准公示,距离 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |