牌号简介 About |
---|
Riblene® FC 20是一种高分子量低密度聚乙烯树脂(LDPE),适用于吹塑薄膜挤出。Riblene® FC 20的特点是具有较高的熔融强度,在挤压过程中具有良好的气泡稳定性。Riblene® FC 20制造的薄膜容易热收缩,具有最佳的机械性能。主要应用Riblene® FC 20推荐用于生产温室薄膜、重型收缩膜和工业袋。 Riblene FC 20 is a high molecular weight low density polyethylene resin (LDPE) suitable for blown film extrusion. Riblene FC 20 is characterised by a high melt strength leading to a good bubble stability during extrusion. Films manufactured by Riblene FC 20 are easily heat shrinkable and characterised by optimum mechanical properties. Main Application Riblene FC 20 is recommended for the production of greenhouse film, heavy duty shrink film and industrial bags. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.922 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.25 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
与自身 - 动态,吹塑薄膜 Self dynamic, blow molded film |
> 0.50 | ISO 8295 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
70 | µm | |
薄膜厚度 film thickness |
60 to 250 µm | ||
拉伸模量 Tensile modulus |
ISO 527-3 | ||
1% 正割,MD,70 µm,吹塑薄膜 1% secant, MD, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
1% 正割,TD,70 µm,吹塑薄膜 1% secant, TD, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,70 µm,吹塑薄膜 MD, yield, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,70 µm,吹塑薄膜 TD, yield, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,70 µm,吹塑薄膜 MD, fracture, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,70 µm,吹塑薄膜 TD, fracture, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,70 µm,吹塑薄膜 MD, fracture, 70 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,70 µm,吹塑薄膜 TD, fracture, 70 µ m, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact 2 |
|||
70 µm,吹塑薄膜 70 µ m, blow molded film 2 |
g | ISO 7765-1/A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 3 |
ISO 6383-2 | ||
MD:70.0 µm MD:70.0 µm |
kN/m | ISO 6383-2 | |
TD:70.0 µm TD:70.0 µm |
kN/m | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,70 µm,吹塑薄膜 45 °, 70 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
70.0 µm,吹塑薄膜 70.0 µ m, blow molded film |
% | ISO 14782 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
3 Blown Film |
【新闻资讯】查看全部
吉林化纤600吨高性能碳纤维项目首条碳化线试车成功
2021-11-03 搜料网资讯: 日前,在吉林化纤凯美克公司碳化车间生产线上,雪白的碳纤维原丝有序穿行,伴随着预氧丝成功产出,600吨高性能碳纤维项目首条碳化线一次试车成功。 作为吉林化纤集 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |