| 牌号简介 About |
|---|
| Solanyl C2002是一种适合挤压的端部化合物。Solanyl C2002可以在传统的挤压生产线上加工。Solanyl C2002是目前使用的可生物降解塑料的竞争性替代品,如PP、HIPS和PS,适用范围广泛。Solanyl C2002可与大多数生物聚酯或淀粉基塑料混合,以降低成本。Solanyl C2002具有自然的手感和外观。Solanyl C2002可生物降解,生物基或植物基含量大于60%。可使用Solanyl C2002的应用包括:消费品和包装农产品热成型应用、杯、盒和托盘、板材和片材基础应用,如管道挤压型材。 Solanyl ® C2002 is an end compound suitable for extrusion. Solanyl ® C2002 can be processed on conventional extrusion lines. Solanyl ® C2002 is a competitive alternative for currently used biodegradable plastics, like PP, HIPS & PS for a wide range of applications. Solanyl ® C2002 can be mixed with most biopolyesters or starch based plastics to reduce costs. Solanyl ® C2002 has a natural feel and look. Solanyl ® C2002 is biodegradable and has a biobased or plant based content of >60%. Applications in which Solanyl ® C2002 can be used are: Consumer goods & Packaging Agriculture products Thermoform applications Cups, boxes & trays Plates and sheets Groundwork applications like pipes Extruded profiles |
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.25 到 1.30 | g/cm³ | ISO 1183 |
|
表观密度 Apparent density |
0.70 到 0.80 | g/cm³ | ISO 60 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
170℃,2.16kg 170℃,2.16kg |
2.0 到 4.0 | g/10min | |
|
螺旋流动长度 Spiral flow length 2 |
15.0 到 30.0 | cm | |
|
收缩率 Shrinkage |
注册或登录后
所有资料免费
|
% | ISO 294-4 |
|
含水量 water content |
注册或登录后
所有资料免费
|
内部方法 | |
|
灰份含量 Ash Content |
注册或登录后
所有资料免费
|
% | 内部方法 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
注册或登录后
所有资料免费
|
||
|
注塑成型 injection molding |
注册或登录后
所有资料免费
|
MPa | |
|
正割,注塑成型 Cutting, injection molding |
注册或登录后
所有资料免费
|
MPa | |
|
拉伸应变 Tensile strain |
注册或登录后
所有资料免费
|
||
|
屈服,注塑成型 Yield, injection molding |
注册或登录后
所有资料免费
|
% | |
|
断裂,注塑成型 Fracture, injection molding |
注册或登录后
所有资料免费
|
% | |
|
弯曲模量 Flexural Modulus |
注册或登录后
所有资料免费
|
||
|
注塑成型 injection molding |
注册或登录后
所有资料免费
|
MPa | ISO 178 |
|
弯曲强度 Flexural Strength |
注册或登录后
所有资料免费
|
||
|
注塑成型 injection molding |
注册或登录后
所有资料免费
|
MPa | ISO 178 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
注册或登录后
所有资料免费
|
||
|
测试 test |
注册或登录后
所有资料免费
|
µm | |
|
拉伸模量 Tensile modulus |
注册或登录后
所有资料免费
|
||
|
MD MD |
注册或登录后
所有资料免费
|
MPa | |
|
TD TD |
注册或登录后
所有资料免费
|
MPa | |
|
拉伸强度 tensile strength |
注册或登录后
所有资料免费
|
||
|
注塑成型 injection molding |
注册或登录后
所有资料免费
|
MPa | ISO 527-2 |
|
MD,断裂 MD, fracture |
注册或登录后
所有资料免费
|
MPa | |
|
TD,断裂 TD, fracture |
注册或登录后
所有资料免费
|
MPa | |
|
MD MD |
注册或登录后
所有资料免费
|
MPa | |
|
TD TD |
注册或登录后
所有资料免费
|
MPa | |
|
拉伸应变 Tensile strain |
注册或登录后
所有资料免费
|
||
|
MD,屈服 MD, yield |
注册或登录后
所有资料免费
|
% | |
|
TD,屈服 TD, yield |
注册或登录后
所有资料免费
|
% | |
|
MD,断裂 MD, fracture |
注册或登录后
所有资料免费
|
% | |
|
TD,断裂 TD, fracture |
注册或登录后
所有资料免费
|
% | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
注册或登录后
所有资料免费
|
||
|
注塑成型 injection molding |
注册或登录后
所有资料免费
|
kJ/m² | ISO 179/1eA |
|
简支梁无缺口冲击强度 Charpy Unnotched Impact strength |
注册或登录后
所有资料免费
|
||
|
注塑成型 injection molding |
注册或登录后
所有资料免费
|
kJ/m² | ISO 179/1eU |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 HDT |
注册或登录后
所有资料免费
|
||
|
1.8 MPa,未退火 1.8 MPa, unannealed |
注册或登录后
所有资料免费
|
℃ | ISO 75-2/A |
|
玻璃化转变温度 Glass transition temperature |
注册或登录后
所有资料免费
|
℃ | DSC |
|
维卡软化温度 Vicat Softening Temperature |
注册或登录后
所有资料免费
|
℃ | ISO 306/A |
|
熔融温度 Melting temperature |
注册或登录后
所有资料免费
|
||
|
DSC DSC |
注册或登录后
所有资料免费
|
℃ | 内部方法 |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Water Activity Water Activity |
注册或登录后
所有资料免费
|
内部方法 | |
| 备注 |
|---|
| 2、模具温度: 25°C, 熔体温度: 170 到 190°C |
|