牌号简介 About |
---|
Solanyl® C1203是一种适用于注塑和压缩成型应用的端部化合物。Solanyl® C1203可在常规生产线上加工。Solanyl® C1203是目前广泛应用的可生物降解塑料和聚烯烃的竞争替代品。Solanyl® C1203拥有自然的感觉和外观。Solanyl® C1203可生物降解,生物基和植物基含量大于28%。 Solanyl® C1203 is an end compound suitable for injection & compression molding applications. Solanyl® C1203 can be processed on conventional lines. Solanyl® C1203 is acompetitive alternative for currently used biodegradable plastics & polyolefins for a wide range of applications. Solanyl® C1203 has a natural feel & look. Solanyl® C1203 is biodegradable with a biobased and plant based content of > 28%. |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
注塑成型 injection molding |
10 到 20 | kJ/m² | ISO 179/1eA |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
注塑成型 injection molding |
> 10 | kJ/m² | ISO 179/1eU |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
注塑 Injection molding |
11 到 21 | kJ/m² | ISO 180-1A |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
注塑 Injection molding |
无断裂 | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
< 55.0 | ℃ | ISO 75-2/B |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Water Activity Water Activity |
内部方法 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,注塑成型 Shaw's D, injection molding |
ISO 868 | ||
拉伸模量 Tensile modulus |
|||
注塑成型 injection molding |
MPa | ||
正割,注塑成型 Cutting, injection molding |
MPa | ||
拉伸强度 tensile strength |
|||
注塑成型 injection molding |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
屈服,注塑成型 Yield, injection molding |
% | ||
断裂,注塑成型 Fracture, injection molding |
% | ||
弯曲模量 Bending modulus |
|||
注塑成型 injection molding |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
注塑成型 injection molding |
MPa | ISO 178 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
表观密度 Apparent density |
g/cm³ | ISO 60 | |
熔体质量流动速率 Melt Flow Rate |
|||
170℃,2.16kg 170℃,2.16kg |
g/10min | 内部方法 | |
190℃,5.0kg 190℃,5.0kg |
g/10min | ISO 1133 | |
熔体体积流动速率 Melt Volume Rate |
|||
190℃,2.16 kg 190℃,2.16 kg |
cm³/10min | ISO 1133 | |
收缩率 Shrinkage rate |
% | ISO 294-4 | |
含水量 water content |
% | 内部方法 | |
熔体表观粘度 Apparent viscosity of melt |
|||
140℃,10.0 sec^-1 140℃,10.0 sec^-1 |
Pa·s | ||
140℃,100 sec^-1 140℃,100 sec^-1 |
Pa·s | ||
140℃,1000 sec^-1 140℃,1000 sec^-1 |
Pa·s | ||
170℃,10.0 sec^-1 170℃,10.0 sec^-1 |
Pa·s | ||
170℃,100 sec^-1 170℃,100 sec^-1 |
Pa·s | ||
170℃,1000 sec^-1 170℃,1000 sec^-1 |
Pa·s |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
为何我国限塑令实行11年,废弃塑料不减反增?
2019-11-13 《国务院办公厅关于限制生产销售使用塑料购物袋的通知》发布于2007年12月31日,是关于生产销售使用塑料购物袋的通知,目的是为了限制和减少塑料袋的使用,遏制白色污染。限塑11年,限塑 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |