牌号简介 About |
---|
PRIMACOR™ 3150是一种乙烯-丙烯酸共聚物,设计用于软包装应用的挤出/共挤涂层和层压树脂。它对金属、纸张和聚乙烯基材具有优异的粘附性,并具有良好的下拉性、热密封性和耐油和耐油脂性。对于挤压/共挤涂层和层压应用,金属、纸张和聚乙烯基材的粘附性符合:美国FDA 21 CFR 177.1310(a)(1)欧盟,第10/2011号,有关完整细节,请参考法规。 PRIMACOR™ 3150 is an ethylene acrylic acid copolymer designed for extrusion/coextrusion coating and laminating resin for flexible packaging applications. It provides excellent adhesion to metallic, paper and polyethylene substrates, and offers good draw- down, heat sealability and oil and grease resistance. For extrusion/coextrusion coating and laminating applications Adhesion to metallic, paper and polyethylene substrates Cost effective sealant or tie resin for foil-based structures Moisture insensitivity Complies with: U.S. FDA 21 CFR 177.1310(a)(1) EU, No 10/2011 Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.924 | g/cm³ | ASTM D792 , ISO 1183 |
熔体质量流动速率 Melt Flow Rate 2 |
|||
190℃,2.16kg 190℃,2.16kg 2 |
11 | g/10min | ASTM D1238,ISO 1133 |
共聚单体含量 Co monomer content 3 |
3.0 | % | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D638 , ISO 527-2 | ||
屈服,模压成型 Yield, molding |
8.79 | MPa | ASTM D638 , ISO 527-2 |
断裂,模压成型 Fracture, molded |
12.3 | MPa | ASTM D638 , ISO 527-2 |
拉伸应变 Tensile strain |
|||
断裂,模压成型 Fracture, molded |
% | ASTM D638 , ISO 527-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 , ISO 306 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 |
备注 |
---|
2 如同在生产时测量的一样。 |
3 通过 Dow 属性方法测量的共聚单体含量,和 ASTM D 4094 相比具有相同的精确性。 |
【新闻资讯】查看全部
科思创 PPG合作推进生物基固化剂清漆涂装
2021-12-12 搜料网资讯: 11月29日,科思创宣布,携手东风汽车集团旗下高端电动品牌岚图汽车与PPG,就生物基清漆涂装解决方案的商业化深入洽谈,旨在加速推进使用部分生物基固化剂的清漆在岚 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |