牌号简介 About |
---|
iRogran A92E 4860是一种高性能聚酯基热塑性聚氨酯,用于挤出和注塑成型应用。iRogran A92E 4860是亨斯迈技术挤压产品系列的一部分,提供了一种特殊设计的柔性材料,具有广泛的加工窗口,适用于制备螺旋管、气动管、皮带和技术模具。性能特点:高拉伸强度、优异的磨损性能、优异的耐水解性、良好的低温柔韧性。 IROGRAN A92E 4860 is a high performance polyester based thermoplastic polyurethane intended for extrusion and injection moulding applications. IROGRAN A92E 4860 is part of the HUNTSMAN technical extrusion product range and offers a specially designed, flexible material with a broad processing window particularly suitable for the preparation of spiral tubing, pneumatic tubing, belting and technical mouldings. PERFORMANCE FEATURES High tensile strength Excellent wear performance Excellent hydrolysis resistance Good low temperature flexibility |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
1.20 | g/cm³ | ASTM D792 |
密度 Density 3 |
1.20 | g/cm³ | DIN 53479 |
熔体体积流动速率 Melt Volume Rate |
|||
210℃,10 kg 210℃,10 kg |
33.0 | cm³/10min | |
收缩率 Shrinkage rate |
|||
MD:注塑成型 MD: Injection molding |
0.90 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
DIN 53505 | ||
邵氏 A,注塑成型 Shaw A, injection molding |
91 | DIN 53505 | |
邵氏 D,注塑成型 Shaw's D, injection molding |
DIN 53505 | ||
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A,注塑成型 Shaw A, injection molding |
ASTM D2240 | ||
邵氏 D,注塑成型 Shaw's D, injection molding |
ASTM D2240 | ||
Abrasion Abrasion 2 |
mm³ | DIN 53516 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
断裂 fracture 2 |
MPa | ASTM D412 | |
断裂 fracture 2 |
MPa | DIN 53504 | |
300% 应变 300% strain 2 |
MPa | DIN 53504 | |
300% 应变 300% strain 2 |
MPa | ASTM D412 | |
100% 应变 100% strain 2 |
MPa | ASTM D412 | |
100% 应变 100% strain 2 |
MPa | DIN 53504 | |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
% | ASTM D412 | |
断裂 fracture 2 |
% | DIN 53504 | |
撕裂强度 tear strength 2 |
kN/m | ASTM D624 | |
撕裂强度 tear strength 2 |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation 2 |
ASTM D395 | ||
23℃,24 hr 23℃,24 hr |
% | ASTM D395 | |
70℃,24 hr 70℃,24 hr |
% | ASTM D395 | |
压缩形变 Compression deformation 2 |
ISO 815 | ||
23℃,24 hr 23℃,24 hr |
% | ISO 815 | |
70℃,24 hr 70℃,24 hr |
% | ISO 815 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
TMA TMA 3 |
Internal Method | ||
Low-High:635.0 µm Low-High:635.0 µm |
℃ | Internal Method | |
Peak:635.0 µm Peak:635.0 µm |
℃ | Internal Method |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Injection Molded |
3 Extruded Film |
【新闻资讯】查看全部
中塑协板片材专业委员会2015年会暨技术交流会纪要
2015-11-24 中国塑协板片材专业委员会2015年会暨技术交流会,于2015年11月3-4日在南京金陵新城酒店召开。会议由中国塑料加工工业协会主办,中国塑协板片材专业委员会、江苏诚盟装备股份有限公司承办。参加会议的有来自全国各地塑料板片材制品生产企业,及与之相关的原料、模具及设备企业、科研院校等单位代表200多人。中国塑料加工工业协会曹俭常务副理事长、南京高新开发区陈千茂副主任、中国塑协板片材专委会任月璋理事长及协会相关部门负责人出席了会议。会议由中国塑协板片材专委会朱山宝常务副理事长主持。 < |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |