牌号简介 About |
---|
BC8400是一种未填充、低粘度、快速凝固的双组分聚氨酯系统。易于使用的1:1混合比(A/B部分),BC8400为用户提供3分钟的工作时间,部件可在30分钟内拆卸。适当固化后,BC 8400将表现出高冲击强度,并产生热塑性类似零件。一些突出的特点包括:无汞、中等耐热性、1:1混合比固化后变白、模具寿命长、冲击强度高、无不良气味、优良的表面处理性能、热塑性外观、每天更多零件 BC8400 is an unfilled, low viscosity, quick setting two component urethane system. An easy to use 1 to 1 mix ratio (Part A/Part B), BC8400 offers the user a 3 minute working time with parts demoldable in as little as 30 minutes. When properly cured, BC 8400 will exhibit high impact strength and yield thermoplastic-like parts. Some outstanding features include the following: Mercury free Moderate heat resistance 1 to 1 mix ratio Turns white upon cure Longer mold life High impact strength No objectionable odor Excellent finishing properties Thermoplastic appearance More parts per day |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.09 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.25 | % | ASTM D2566 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
72 | J/m | ASTM D256 |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颜色 colour |
|||
-- -- 2 |
Amber | ||
-- -- 3 |
Opaque | ||
重量混合比(PBW) Weight Mix Ratio (PBW) |
|||
Part A Part A |
|||
体积混合比(PBV) Volume Mixing Ratio (PBV) |
|||
Part B Part B |
|||
粘度 viscosity |
|||
-- -- 2 |
Pa·s | ||
-- -- 4 |
Pa·s | ||
-- -- 3 |
Pa·s | ||
胶凝时间 Gelation time |
min | ASTM D2471 | |
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸断裂强度 Tensile fracture strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲断裂强度 Bending fracture strength |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
24 hrs @ room temp. + 1 hr @ 150°F 24 hrs @ room temp. + 1 hr @ 150°F |
℃ | ||
7 days @ room temp. 7 days @ room temp. |
℃ | ||
脱模时间 stripping time |
|||
25℃ 25℃ |
min |
备注 |
---|
2、Part A |
3、Part B |
4、Mixed |
【新闻资讯】查看全部
中共中央:建立健全碳达峰、碳中和标准,提升重点产品能耗限额要求
2021-10-11 搜料网资讯: 中共中央、国务院印发《国家标准化发展纲要》。其中提到,建立健全碳达峰、碳中和标准。加快节能标准更新升级,抓紧修订一批能耗限额、产品设备能效强制性国家标 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |