牌号简介 About |
---|
高热通用级聚苯乙烯无矿物油,复合强度高,耐热性好。采用引发聚合法生产。用途:用于照明器具用挤塑聚苯乙烯泡沫塑料的制造。也推荐用于制造大型家电零件(透明防尘件等)和文具。 General purpose polystyrene with high thermal stability, without addition of mineral oil, combines strength and high heat resistance. It is produced by initiated bulk polymerization. It is intended for manufacture of foamed extrusion and thick-gage sheets of lighting equipment. It is also recommended for manufacture of big parts of household electrical appliances (transparent dustproof, etc.) and office supplies. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
3.0 到 5.0 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂 fracture |
45.0 | MPa | ASTM D638 |
弯曲强度 bending strength |
90.0 | MPa | ASTM D790 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
97.0 | ℃ | ASTM D1525 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Residual Styrene Residual Styrene 2 |
0.050 | % |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 TU 2214-126-05766801 |
【新闻资讯】查看全部
环己酮肟绿色合成有新途
2022-05-13 5月6日,国际顶级学术期刊Science刊发了上海交通大学化学化工学院陈立桅教授、刘晰研究员等人合作的科研成果原位生成过氧化氢用于高效催化由环己酮合成环己酮肟。 该研究成功将原 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |