牌号简介 About |
---|
ALCOM® LDX PC 1000 UV 15064 CC1125-15是一种聚碳酸酯(PC)产品,含有的填充物为填料。 它可以通过挤出或注射成型进行加工, 典型应用领域为:照明设备。 特性包括: 阻燃/额定火焰 通过 ROHS 认证 Light Diffusion 紫外线稳定 ALCOM® LDX PC 1000 UV 15064 CC1125-15 is a Polycarbonate (PC) product filled with filler. It can be processed by extrusion or injection molding and is available in Asia Pacific, Europe, or North America. Typical application: Lighting Applications. Characteristics include: Flame Rated RoHS Compliant Light Diffusion UV Stabilized |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.19 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
7.00 | cm³/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
2400 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
|||
屈服 yield |
66.0 | MPa | |
-- -- |
66.0 | MPa | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ||
断裂 fracture |
% | ||
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
3.50% 应变 3.50% strain |
MPa | ||
-- -- |
MPa | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-- -- |
kJ/m² | ||
-40℃ -40℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-- -- |
|||
-40℃ -40℃ |
|||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
|||
0.75 mm 0.75 mm |
|||
灼热丝可燃性指数 Glowing wire flammability index |
|||
1.0 mm 1.0 mm |
℃ | ||
2.0 mm 2.0 mm |
℃ | ||
3.0 mm 3.0 mm |
℃ | ||
4.0 mm 4.0 mm |
℃ | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透光率 Transmittance 2 |
|||
总计,1000 µm Total, 1000 µ m |
% | ||
总计,2000 µm Total, 2000 µ m |
% | ||
总计,3000 µm Total, 3000 µ m |
% | ||
总计,4000 µm Total, 4000 µ m |
% | ||
雾度 Haze 2 |
|||
1000 µm 1000 µm |
% | ||
2000 µm 2000 µm |
% | ||
3000 µm 3000 µm |
% | ||
4000 µm 4000 µm |
% | ||
Half Power Angle Half Power Angle 2 |
|||
1.00 mm 1.00 mm |
° | ||
2.00 mm 2.00 mm |
° | ||
3.00 mm 3.00 mm |
° | ||
4.00 mm 4.00 mm |
° |
备注 |
---|
2. A, 2° |
【新闻资讯】查看全部
天策新资料公司自主研收回MPCF
2018-07-25 陕西天策新材料科技有限公司自主研发的连续纺丝技术制备高性能沥青基碳纤维(MPCF),在国内率先打通工艺流程并实现小批量生产,年产能超过2吨。此举将打破国外技术封锁,为我国航天航空和国防领域应用高端新材料奠定基础。 “采用连续式预氧化、碳化、石墨化工艺生产MPCF,我们是目前国内唯一全流程贯通并实现小批量供货的企业。”天策科技公司副总经理张鸿翔告诉记者,他们通过与北京化工大学合作,分别采用萘合成和石油渣油、煤焦油调制,开发出了MPCF纺丝专用的中间相沥青。经过熔融纺丝制成中间 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名:搜料网-ALCOM® LDX PC 1000 UV 15064 CC1125-15证书
发送至:(多个地址,中间以逗号隔开)
发送一份副本给我:您还没有填写邮箱!(点击完善资料)