牌号简介 About |
---|
Alkatuff® LL501是一种己烯线性低密度聚乙烯共聚物,设计用于各种通用薄膜应用。Alkatuff® LL501与工艺稳定包一起配制,但不含滑动或防阻塞添加剂。薄膜挤出:Alkatuff® LL501适用于工业、农业和重型薄膜等一般用途。Alkatuff® LL501也非常适合用于混合应用。更高的硬度Alkatuff® LL501可以改善薄膜处理转换和包装操作。如果预期的应用涉及间歇性到长时间暴露在阳光下,则应考虑添加紫外线稳定剂。 Alkatuff LL501 is a hexene linear low density polyethylene copolymer designed for a variety of general purpose film applications. Alkatuff LL501 is formulated with a process stabilisation package but contains no slip or antiblocking additives. Film Extrusion: Alkatuff LL501 is intended for general purpose applications such as industrial, agricultural and heavy duty films. Alkatuff LL501 is also ideally suited for use in blending applications. The higher stiffness of Alkatuff LL501 can improve film handling in converting and packaging operations. Addition of a UV stabiliser should be considered where the intended application involves intermittent to extended exposure to sunlight. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.925 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
50 | µm | |
割线模量 Secant modulus 2 |
|||
2% 正割,MD:50 µm 2% secant, MD: 50 µ m |
240 | MPa | |
2% 正割,TD:50 µm 2% secant, TD: 50 µ m |
270 | MPa | |
拉伸强度 tensile strength 3 |
|||
MD,屈服,50 µm MD, yield, 50 µ m |
MPa | ||
TD,屈服,50 µm TD, yield, 50 µ m |
MPa | ||
MD,断裂,50 µm MD, fracture, 50 µ m |
MPa | ||
TD,断裂,50 µm TD, fracture, 50 µ m |
MPa | ||
拉伸应变 Tensile strain 3 |
|||
MD,断裂,50 µm MD, fracture, 50 µ m |
% | ||
TD,断裂,50 µm TD, fracture, 50 µ m |
% | ||
落锤冲击 Drop hammer impact 4 |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film 4 |
g | ASTM D1709 | |
撕裂强度 tear strength |
|||
MD,50 µm MD,50 µm |
N | ||
TD,50 µm TD,50 µm |
N | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,50.0 µm,吹塑薄膜 45 °, 50.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
备注 |
---|
2、20 mm/min |
3、500 mm/min |
4、F50 |
【新闻资讯】查看全部
橡塑板块行情分化橡胶强于塑料
2017-01-17 2016年对橡胶及塑料行业来说是至关重要的一年,从市场走势来看,一扫2015年全线下跌的阴霾,全线飘红,而且多数产品涨幅偏强,三分之二的产品涨幅超过30%。而业内人士表示,2017年橡塑市场并不乐观,出现分化的可能性较大,橡胶可能会维持偏强的走势,塑料的表现可能会弱于橡胶。 市场不乐观 据生意社监测,2016年大宗商品价格涨跌榜中橡塑板块监测的22种商品价格全线上涨,价格涨幅前3的商品分别为顺丁橡胶(141.99%)、丁苯橡胶(1502)(115.68%)、 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |