牌号简介 About |
---|
Jam PE 12X01是一种线性低密度聚乙烯产品,。 它,在非洲和中东有供货。 典型应用领域为:电影。 主要特性为:丁烯共聚单体。 12X01 is a HP-LLDPE blown film grade of excellent processability and good film strength combined with low gels. Features Superbutene Excellent processability Good film strength Low gels Application Blown film grade |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.912 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.95 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
25.0 到 180 | µm | |
测试 test |
25 | µm | |
割线模量 Secant modulus |
ASTM D882 | ||
2% 正割,MD:25 µm,吹塑薄膜 2% secant, MD: 25 µ m, blow molded film |
190 | MPa | ASTM D882 |
2% 正割,TD:25 µm,吹塑薄膜 2% secant, TD: 25 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,25 µm,吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ASTM D882 | |
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:25 µm,吹塑薄膜 MD: 25 µ m, blow molded film |
g | ASTM D1922 | |
TD:25 µm,吹塑薄膜 TD: 25 µ m, blow molded film |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,25 µm,吹塑薄膜 45 °, 25 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Blow(up Ratio) Blow(up Ratio) |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
工程塑料企业Polyscope推出XIRAN添加剂新牌号
2016-07-01 近日,Polyscope公司扩充了其XIRAN耐热添加剂产品系列,增添了新牌号。新牌号的玻璃化转变温度(Tg)为198˚C,进一步提升了耐热性。此外,公司将在K 2016展会上庆祝公司成立10周年。 在公司的K 2016展前新闻简介会上,Polyscope公司工程塑料业务部总监Ferdi Faas介绍了新牌号。他解释说,新牌号在高加工温度条件下使用,与苯乙烯类聚合物具有优异的兼容性。 新牌号的推出证明Polyscope公司坚持与OEM紧密合作的战略路线,正如 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |