牌号简介 About |
---|
PA610挤出级,柔韧性高。增韧和塑化。热稳定。黑色。适用于管道、型材和电缆护套的挤压。它在低温下也能提供更好的抗冲击性。这一等级是部分可再生来源(60%的基础聚合物按重量计)。 PA610 extrusion grade with high flexibility. Toughened and plasticized. Heat stabilized. Black colour. Suitable for extrusion of pipes, profiles and cable jackets. It offers improved impact resistance, also at low temperatures. This grade is partially renewably-sourced (60% of base polymer by weight). |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.03 | g/cm³ | |
吸水率 Water absorption rate |
|||
饱和,23℃,2.00 mm Saturation, 23 ℃, 2.00 mm |
2.0 | % | |
平衡,23℃,50% RH,2.00 mm Equilibrium, 23 ℃, 50% RH, 2.00 mm |
0.90 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
470 | MPa | |
拉伸强度 tensile strength |
|||
屈服 yield |
24.0 | MPa | |
标称拉伸断裂应变 Nominal tensile fracture strain |
% | ||
弯曲模量 Bending modulus 2 |
MPa | ||
弯曲强度 bending strength 2 |
MPa | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ||
熔融温度 Melting temperature 3 |
℃ |
备注 |
---|
2、2.0 mm/min |
3、10°C/min |
【新闻资讯】查看全部
伊士曼销售和盈利创纪录
2022-02-16 近日,伊士曼发布2021年第四季度和全年财务报告。报告显示,公司全年销售收入与调整后每股盈利均创下纪录。由于持续运用创新型增长模式,公司取得快于终端市场的增长速度。 财 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |