牌号简介 About |
---|
特点和优点组成:偏氟乙烯和六氟丙烯的二元聚合物中等粘度工艺目标:压缩和转移成型、粘合和压延专有的复合固化技术从模具中去除复杂零件(如轴密封)的优异热撕裂强度。 Features and Benefits Composition: di-polymer of vinylidene fluoride and hexafluoropropylene Medium viscosity Process targets: compression and transfer molding, bonding and calendering Proprietary incorporated cure technology Excellent hot tear strength for removing complex parts from mold (such as shaft seals) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.80 | g/cm³ | |
门尼粘度 Mooney viscosity |
|||
ML 1+10,121℃ ML 1+10,121℃ |
34 | MU | |
氟含量 Fluorine content |
66 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
75 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
12.9 | MPa | |
100% 应变 100% strain |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ||
压缩形变 Compression deformation |
|||
200℃,70 hr 200℃,70 hr |
% | ASTM D395B | |
MH(177℃) MH(177℃) |
J | ||
ML(177℃) ML(177℃) |
J | ||
t'50(177℃) t'50(177℃) |
min | ||
t'90(177℃) t'90(177℃) |
min | ||
ts2(177℃) ts2(177℃) |
min | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Tr10 Tr10 |
℃ | ASTM D1329 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
投资5.1亿元!万华宁波高性能材料研究院竣工投用
2021-08-31 搜料网资讯: 8月29日上午,大榭开发区万华宁波高性能材料研究院(以下简称:万华研究院)竣工投用。 市委常委、党工委书记、管委会主任梁群见证项目竣工投用,市委常委、市政府 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |