牌号简介 About |
---|
涂层等级;不含任何抗水解剂;本产品按照良好生产规范(第2023/2006号法规(EC)中定义的GMP)制造,因此限制了与食品接触使用的适宜性。请参阅我们的单独证书:http://www.tpu.covestro.com/en/library/certificates/food contact.aspx.;application;纺织涂料 Coating grade; does not contain any anti-hydrolysis agent; This product is manufactured under Good Manufacturing Practice (GMP defined in Regulation (EC) No. 2023/2006) and is therefore limited suitability for use with food contact. Please refer our separate certificate at http://www.tpu.covestro.com/en/Library/Certificates/Food-Contact.aspx.; Application; Textile coating |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.21 | g/cm³ | ISO 1183 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
撕裂强度 tear strength 4 |
|||
23℃ 23℃ 4 |
77 | kN/m | ISO 34-1 |
压缩形变 Compression deformation |
|||
23℃,72 hr 23℃,72 hr |
28 | % | |
70℃,24 hr 70℃,24 hr 3 |
62 | % | |
70℃,24 hr 70℃,24 hr 5 |
44 | % | |
回弹性 Resilience |
% | ISO 4662 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,1 秒,23℃ Shore A, 1 second, 23 ℃ |
|||
邵氏 D,1 秒,23℃ Shore D, 1 second, 23 ℃ |
|||
拉伸强度 tensile strength 2 |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ||
10% 应变,23℃ 10% strain, 23 ℃ |
MPa | ||
50% 应变,23℃ 50% strain, 23 ℃ |
MPa | ||
100% 应变,23℃ 100% strain, 23 ℃ |
MPa | ||
300% 应变,23℃ 300% 应变, 23°C |
MPa | ||
拉伸应变 Tensile strain 2 |
|||
断裂,23℃ Fracture, 23 ℃ 2 |
% | DIN 53504 | |
拉伸储能模量 Tensile storage modulus |
|||
-20℃ -20℃ |
GPa | ||
20℃ 20℃ |
GPa | ||
60℃ 60℃ |
GPa | ||
|
mm³ | ISO 4649 |
备注 |
---|
2、200 mm/min |
3、Method A |
4、500 mm/min |
5、Method C |
【新闻资讯】查看全部
三菱化学与泰国PTT联手开发成功新型可分解塑胶资料
2018-11-08 近期,日本三菱化学控股和泰国国家石油公司PTT联手开发出新型的可分解塑胶材料,把现有的两种生物可分解塑胶结合形成更加强韧的新素材,而且暴露在空气和水中就可以分解,而且可以让塑料吸管制造商沿用现有的模具就可以生产出环保类型的吸管。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |