牌号简介 About |
---|
PBT+PET,20%玻璃纤维,注塑成型,提高冲击强度,低翘曲倾向,改善表面光洁度,紫外线稳定 POCAN® TS3221 901510 PBT+PET, 20 % glass fibers, injection molding, improved impact strength, low tendency to warp, improved surface finish, UV-stabilized POCAN® TS3221 901510 PBT+PET, 20 % glass fibers, injection molding, improved impact strength, low tendency to warp, improved surface finish, UV-stabilized POCAN® TS3221 901510 PBT+PET, 20 % glass fibers, injection molding, improved impact strength, low tendency to warp, improved surface finish, UV-stabilized |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.39 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.70 | g/cm³ | ISO 60 |
熔体体积流动速率 Melt Volume Rate |
|||
270℃,5 kg 270℃,5 kg |
18.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 2577 | ||
TD:270℃,2.0 mm TD:270℃,2.0 mm 2 |
0.70 | % | ISO 2577 |
TD:120℃,2.0 mm,4 hrs TD:120℃,2.0 mm,4 hrs 3 |
0.10 | % | ISO 2577 |
MD:270℃,2.0 mm MD:270℃,2.0 mm 2 |
% | ISO 2577 | |
MD:120℃,2.0 mm,4 hrs MD:120℃,2.0 mm,4 hrs 3 |
% | ISO 2577 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus 4 |
|||
23℃ 23℃ 4 |
MPa | ISO 178-A | |
弯曲强度 bending strength 4 |
|||
23℃ 23℃ 4 |
MPa | ISO 178-A | |
弯曲应变 Bending strain 5 |
% | ISO 178/A | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ISO 180/1U | ||
-30℃ -30℃ |
kJ/m² | ISO 180/1U | |
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B120 B120 |
℃ | ISO 306/B120 | |
熔融温度 Melting temperature 6 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
ISO 11359-2 | ||
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
ISO 7792 |
备注 |
---|
2 60x60x2mm, 90°C MT, 600 bar |
3 60x60x2mm |
4 2.0 mm/min |
5 2 mm/min |
6 10°C/min |
【新闻资讯】查看全部
革新发力 工业企业开好头
2018-03-30 国家统计局27日发布的工业企业财务数据显示,1―2月份,全国规模以上工业企业利润同比增长16.1%,增速比2017年12月份加快5.3个百分点,保持了快速增长势头,工业企业效益开局向好。 企业利润增长加快,采矿业一马当先。1―2月份,采矿业实现利润总额877.9亿元,同比增长42.1%;电力、热力、燃气及水生产和供应业实现利润总额711.1亿元,增长35.2%;制造业实现利润总额8100亿元,增长12.5%。在41个工业大类行业中,29个行业利润总额同比增加,1个行业持平, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |