牌号简介 About |
---|
PA 6,30%玻璃纤维/碳纤维,注塑成型,热老化稳定,提高导电率 Durethan® BCF30XH3.0 000000 (Dry) PA 6, 30 % glass fibers/carbon fibers, injection molding, heat-aging stabilized, improved electrical conductivity Durethan® BCF30XH3.0 000000 PA 6, 30 % glass fibers/carbon fibers, injection molding, heat-aging stabilized, improved electrical conductivity Durethan® BCF30XH3.0 000000 PA 6, 30 % glass fibers/carbon fibers, injection molding, heat-aging stabilized, improved electrical conductivity |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.34 | g/cm³ | |
收缩率 Shrinkage rate |
|||
TD:120℃,2.0 mm TD:120℃,2.0 mm 2 |
0.10 | % | |
TD:280℃,2.0 mm TD:280℃,2.0 mm 3 |
0.75 | % | |
MD:120℃,2.0 mm MD:120℃,2.0 mm 2 |
0.050 | % | |
MD:280℃,2.0 mm MD:280℃,2.0 mm 3 |
0.25 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ||
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ||
弯曲模量 Bending modulus 4 |
|||
23℃ 23℃ 4 |
MPa | ||
弯曲强度 bending strength 4 |
|||
23℃ 23℃ |
MPa | ||
3.50% 应变,23℃ 3.50% strain, 23 ℃ |
MPa | ||
弯曲应变 Bending strain 5 |
% | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
|||
-30℃,冲击总贯穿能量 -30 ℃, total impact penetration energy |
J | ||
23℃,冲击总贯穿能量 23 ℃, total impact penetration energy |
J | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ||
维卡软化温度 Vicat Softening Temp |
℃ | ||
熔融温度 Melting temperature 6 |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23~55℃ MD:23~55℃ |
1/℃ | ||
TD:23~55℃ TD:23~55℃ |
1/℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ||
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
备注 |
---|
2. 60x60x2mm, 4 hr |
3. 60x60x2mm, 80°C MT, 600 bar |
4. 2.0 mm/min |
5. 2 mm/min |
6. 10°C/min |
【新闻资讯】查看全部
大型塑料3D打印领航机械建模
2017-11-02 塑料与3D打印有着密切的关系,材料方面最受欢迎包括PLA材料,具有相对较低的打印挑战。其他复合材料可用于更高级的应用,并具有更好的机械性能。 3D打印行业领先的解决方案之一是大型3D打印。塑料产品的大型3D打印机主要基于熔融挤出技术,工艺可靠,易于使用和维护。 现在出现了一个明显的话题:大型3D打印的应用领域在哪里,使用大型3D打印有什么好处? ・设计与概念建模 对于设计领域来说,尺寸经常限制了设计产品的快速制造,有了大型零件 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |