![](/page/pc/images/result/downloads-img2.png)
物性表自定义
公司信息及水印
公司信息及水印
![](/page/pc/images/result/downloads-img4.png)
![](/page/pc/images/result/downloads-img1.png)
下载中文物性表
![](/page/pc/images/result/downloads-tag3.png)
![](/page/pc/images/result/downloads-img1.png)
下载英文物性表
![](/page/pc/images/result/downloads-tag3.png)
![](/page/pc/images/result/downloads-img1.png)
下载原厂物性表
![](/page/pc/images/result/downloads-tag3.png)
![](/page/pc/images/result/downloads-img3.png)
邮件发送/他人
牌号简介 About |
---|
PBT,20%玻璃球,注塑成型,不易翘曲,改善表面光洁度 POCAN® B7425 000000 PBT, 20 % glass spheres, injection molding, low tendency to warp, improved surface finish POCAN® B7425 000000 PBT, 20 % glass spheres, injection molding, low tendency to warp, improved surface finish POCAN® B7425 000000 PBT, 20 % glass spheres, injection molding, low tendency to warp, improved surface finish |
产品描述 Product Description
厂家:德国朗盛 LANXESS
类别:PBT polybutylene terephthalate
加工条件:注射成型 Injection Molding
性能特点: 低翘曲性; 表面光泽度好; Low warping,Good surface appearance
填料:玻璃珠 20
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.44 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.90 | g/cm³ | ISO 60 |
熔体体积流动速率 Melt Volume Rate |
|||
260℃,5 kg 260℃,5 kg |
35.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
TD:120℃,2.0 mm TD:120℃,2.0 mm 3 |
0.20 | % | |
TD:260℃,2.0 mm TD:260℃,2.0 mm 4 |
2.1 | % | |
MD:120℃,2.0 mm MD:120℃,2.0 mm 3 |
% | ||
MD:260℃,2.0 mm MD:260℃,2.0 mm 4 |
% | ||
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ||
粘度值 Viscosity value |
|||
降低的粘度 Reduced viscosity |
ml/g | ISO 1628 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
200℃ 200℃ |
IEC 60695-10-2 | ||
熔融温度 Melting temperature 7 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23~55℃ MD:23~55℃ |
1/℃ | ||
TD:23~55℃ TD:23~55℃ |
1/℃ | ||
导热系数 Thermal conductivity coefficient |
|||
23℃ 23℃ |
W/m/K | ISO 8302 | |
相对温度指数 Relative temperature index |
℃ | UL 746 | |
电气性能 Electrical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
Halving Interval Halving Interval |
|||
介电强度 Dielectric strength |
℃ | ||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | IEC 60243-1 | |
拉伸冲击强度 Tensile impact strength |
℃ | ||
拉伸强度 tensile strength |
℃ | ||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/5 | |
温度指数 Temperature index |
|||
介电强度,20000 hr Dielectric strength, 20000 hr |
℃ | ||
拉伸冲击强度,20000 hr Tensile impact strength, 20000 hr |
℃ | ||
拉伸强度,20000 hr Tensile strength, 20000 hr |
℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
相对电容率 Relative permittivity |
|||
23℃,100 Hz 23℃,100 Hz |
|||
23℃,1 MHz 23℃,1 MHz |
|||
耗散因数 Dissipation factor |
|||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
US FMVSS302 US FMVSS302 |
ISO 3795 | ||
阻燃等级 Flame retardant level |
|||
0.75 mm 0.75 mm |
|||
1.50 mm 1.50 mm |
|||
灼热丝可燃性指数 Glowing wire flammability index |
|||
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
极限氧指数 Extreme oxygen index 8 |
% | ISO 4589-2 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
电解腐蚀 Electrolytic corrosion |
|||
23℃ 23℃ |
IEC 60426 | ||
ISO Shortname ISO Shortname |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
球压硬度 Ball hardness |
MPa | ISO 2039-1 | |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/5 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1 hr 1 hr |
MPa | ||
1000 hr 1000 hr |
MPa | ||
弯曲模量 Bending modulus 5 |
|||
23℃ 23℃ 5 |
MPa | ISO 178-A | |
弯曲强度 bending strength 5 |
|||
23℃ 23℃ |
MPa | ||
3.50% 应变,23℃ 3.50% strain, 23 ℃ |
MPa | ||
弯曲应变 Bending strain 6 |
% | ISO 178/A |
备注 |
---|
3. 60x60x2mm, 4 hr |
4. 60x60x2mm, 80°C MT, 600 bar |
5. 2.0 mm/min |
6. 2 mm/min |
7. 10°C/min |
8. 程序 A |
【新闻资讯】查看全部 ![]()
亨斯迈用废旧塑料瓶生产聚氨酯原料
2020-12-05 搜料网资讯: 聚氨酯的用途非常广泛。这种由多元醇与二异氰酸酯反应形成的材料可以制成滑板轮、汽车的刚性结构、床垫的记忆泡沫以及冰箱和建筑物的隔热材料。但是,聚氨酯的性 |
亨斯迈用废旧塑料瓶生产聚氨酯原料 搜料网资讯:![]() 聚氨酯的用途非常广泛。这种由多元醇与二异氰酸酯反应形成的材料可以制成滑板轮、汽车的刚性结构、床垫的记忆泡沫以及冰箱和建筑物的隔热材料。但是,聚氨酯的性质—由分子紧密结合且通常不可逆地与交联物结合而成的特性,与可再次熔化的热塑性塑料如聚对苯二甲酸乙二醇酯(PET)或聚丙烯(PP)相比,它的回收是一项挑战。 亨斯迈正在以一种有助于解决更广泛的塑料废物问题的方式使聚氨酯更具可持续性:使用从回收塑料中提取的多元醇。 该公司近日在台湾开设了一家工厂,用消费后的聚酯瓶生产Terol芳香族聚酯多元醇。这座2.2万吨/年的工厂是其第二个使用该技术的工厂。亨斯迈于2013年开始在休斯敦运营第一家,该公司表示,自那时起,该公司在休斯敦的消费量相当于50亿个PET瓶。 塑料回收中的一个长期问题是降级回收,即塑料被转化成比原来用途更不值钱的东西。亨斯迈聚氨酯技术与创新全球副总裁Mumick称,Terol为升级循环的一个例子,因为可回收的聚合物被用于绝缘等应用中,有助于多年节约能源。“当所有这些东西开始累积起来,它们就成为一个非常好的可持续发展故事,”Mumick说。 “其中含有回收的成分吸引了工业客户,许多工业客户的目标是在他们自己的。 现在亨斯迈已经在台湾建立了工厂,下一步可能包括在欧洲建立工厂。Mumick表示:“如果未来10年市场继续需要该产品,我们能够以每年10%的速度增长。” |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。