牌号简介 About |
---|
用于电线绝缘和电缆护套等应用中评估的非卤化阻燃柔性Noryl挤压级。优异的阻燃性能,拉伸伸长平衡,能够达到VW-1的性能和UL 1581规定的105C温度等级。肖氏硬度A。通常在标准挤压设备上进行的加工。使用0.12 mm x 20铜绞线对2.0 mm电线进行的UL 1581试验。 Non-halogenated flame retardant Flexible NORYL extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Excellent flame retardant performance with balanced tensile elongation, capable of VW-1 performance and 105C temperature rating as defined by UL 1581. 87 Shore A hardness. Processing typically conducted on standard extrusion equipment. UL 1581 tests conducted on 2.0mm wire with 0.12mm X 20 stranded coppoer conductor. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:PPO(PPE)+TPE PPO(PPE)+TPE
用途:电气/电子应用领域;电子显示器;
加工条件:挤出涂层
性能特点: 无卤; 阻燃; 韧性好; Good flexibility,Halogen free,Flame Characteristics
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.03 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
250℃,10.0kg 250℃,10.0kg |
16 | g/10min | ASTM D1238 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
< -40.0 | ℃ | ASTM D746 |
UL温度额定值 UL temperature rating 7 |
105 | ℃ | UL 1581 |
Heat Deformation(121℃) Heat Deformation(121℃) 8 |
10 | % | UL 1581 |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
2 mm,在油中 2 mm in oil |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
|||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
灼热丝可燃性指数 Glowing wire flammability index |
|||
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
VW-1 VW-1 2 |
UL 1581 | ||
烟雾密度 Smoke density 9 |
|||
Flaming,Ds max:500.0 µm Flaming,Ds max:500.0 µm |
|||
Non-Flaming,Ds max:500.0 µm Non-Flaming,Ds max:500.0 µm |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,30 秒 Shore A, 30 seconds |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
断裂 fracture 2 |
MPa | UL 1581 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂,136℃ Fracture, 136 ℃ 4 |
MPa | UL 1581 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 2 |
% | UL 1581 | |
断裂 fracture 3 |
% | ASTM D638 | |
断裂,136℃ Fracture, 136 ℃ 5 |
% | UL 1581 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 6 |
|||
100 mm跨距 100 mm span |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 |
备注 |
---|
2. 2.0 mm wire with 0.12 mm x 20 stranded copper |
3. 类型 1, 50 mm/min |
4. After 7 days. Tested on 2.0 mm wire with 0.12 mm x 20 stranded copper |
5. 6 days, 2.0 mm wire with 0.12 mm x 20 stranded copper |
6. 13 mm/min |
7. 2.0mm wire with 0.12 mm x 20 stranded copper |
8. 250g, 2.0 mm wire with 0.12 mm x 20 stranded copper |
9. Plaque |
【新闻资讯】查看全部
盛情邀请于11月6-8日与你相约狮山,共享塑膜盛会!
2022-05-24 塑料膜材料行业盛会 第十七届国际塑料工业新材料新工艺新装备行业峰会 (以下简称狮山塑料峰会),2022年11月6-8日与您相约 南国桃园枫丹白鹭酒店 (广东省佛山市南海区狮山镇南国 |
盛情邀请于11月6-8日与你相约狮山,共享塑膜盛会! 塑料膜材料行业盛会——第十七届国际塑料工业新材料新工艺新装备行业峰会(以下简称狮山塑料峰会),2022年11月6-8日与您相约南国桃园枫丹白鹭酒店(广东省佛山市南海区狮山镇南国桃园风景区内),不见不散!
17载春秋,从青丝到华发;17载坚守,只为我国塑膜产业健康持续稳定发展;17载沉淀,狮山塑料峰会早已深入我国塑膜业界人士灵魂深处。
来自塑膜材料、加工及检测设备、塑膜、科研院所、协会等行业的顶级企业和专家、教授等,累计带来专业技术报告500+个,累计参会人数7000+。
传递业界先进工艺技术,探求行业/企业发展新模式和途径,促进业内企业资源共享,参会企业与行业代表互动交流、分享、沟通行业最新信息,促进产业链上下游垂直化合作、专业化发展。
2022年11月6-8日,老地方与您再次相约,不见不散! |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。