牌号简介 About |
---|
聚碳酸酯(PC)树脂是一种非填充树脂,适用于注塑和挤出。这种非氯化、非溴化阻燃PC的UL-94V0额定值为1.0 mm/5VA额定值为3.0 mm,并且紫外线稳定(F1额定值)提供了额外的耐候性。Lexan CFR7630树脂有透明和不透明两种颜色。 LEXAN CFR7630 Polycarbonate (PC) resin is a non-filled resin, suitable for injection molding and extrusion. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.0 mm / 5VA rating at 3.0mm and is UV stabilized (F1 rating) providing additional weathering capability. LEXAN CFR7630 resin is available in transparent and opaque colors. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- |
1.19 | g/cm³ | ASTM D792 |
-- -- |
1.20 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
5.0 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
5.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.55 到 0.75 | % | |
TD:3.2 mm TD:3.2 mm |
% | ||
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ||
室外适用性 Outdoor applicability |
UL 746C | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 3 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield 4 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
断裂 fracture 4 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield 4 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus |
|||
50 mm跨距 50 mm span 5 |
MPa | ASTM D790 | |
-- -- 6 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- 6 , 7 |
MPa | ISO 178 | |
屈服,50 mm跨度 Yield, 50 mm span 5 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 8 |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 8 |
|||
-30℃ -30℃ |
|||
23℃ 23℃ |
|||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ 9 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 9 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-30℃ -30℃ |
|||
23℃ 23℃ |
|||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,100 mm跨距 0.45 MPa, unannealed, 100 mm span 10 |
℃ | ISO 75-2/Be | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,100 mm跨距 1.8 MPa, unannealed, 100 mm span 10 |
℃ | ISO 75-2/Ae | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 11 | |
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
123~127℃ 123~127℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:23~80℃ MD:23~80℃ |
1/℃ | ISO 11359-2 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:23~80℃ TD:23~80℃ |
1/℃ | ISO 11359-2 | |
相对温度指数 Relative temperature index |
℃ | UL 746 | |
电气性能 Electrical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电常数 Dielectric constant |
|||
1.10 GHz 1.10 GHz |
ASTM ES7-83 | ||
耗散因数 Dissipation factor |
|||
1.1 GHz 1.1 GHz |
ASTM ES7-83 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.00 mm 1.00 mm |
|||
3.00 mm 3.00 mm |
|||
灼热丝可燃性指数 Glowing wire flammability index |
|||
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透光率 Transmittance |
|||
1000 µm 1000 µm |
% | ||
2000 µm 2000 µm |
% | ||
3000 µm 3000 µm |
% |
备注 |
---|
3. 50 mm/min |
4. 类型 1, 50 mm/min |
5. 1.3 mm/min |
6. 2.0 mm/min |
7. at Yield |
8. 80*10*3 sp=62mm |
9. 80*10*3 mm |
10. 120*10*4 mm |
11. 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
科思创:立足中国 看好医疗新动力汽车的开展
2016-06-02 德国材料生产商科思创致力于将在中国的技术创新与世界共享。科思创将聚氨酯树脂与织物玻璃纤维向结合,开发了生产风力涡轮机刀片的新工艺。这种有三帧折叠叶片的刀片总长40米左右,可一次成型,相较传统生产方法,更加高效,并且,生产过程中排放的挥发性有毒气体也相应减少。科思创在中国有一个团队,专门负责亚太地区的技术创新。恰逢中国发展绿色经济的风头正健,风力发电市场潜力巨大,该团队将聚氨酯添加到风电叶片中,增强产品性能。中国,几乎是所有消费类产品最大的市场。它的风能设备市场,截至2016年底,风能发电量 |
科思创:立足中国 看好医疗新动力汽车的开展 法国原材料制造商科思创着眼于将在中国的技术革新与全球共享资源。科思创将聚氨酯胶粘剂与纺织物玻纤向融合,开发设计了生产制造风力发电机刀头的新技术新工艺。这类有三帧伸缩叶子的刀头全长40米长,可一次成形,相较传统式生产制造方式,更为高效率,而且,加工过程中排污的挥发物有害气体也相对降低。科思创在中国有一个精英团队,专业承担亚洲地区的技术革新。正逢中国发展趋势绿色发展的可谓是正健,风能发电市场发展潜力极大,该精英团队将聚氨酯材料加上到风电叶片中,提高产品特性。中国,基本上是全部消费性产品较大 的市场。它的风力设备市场,截止2016年底,地热发电量预估达到250KW。 上年,中国市场销售量占科思创总销售量的15%。上年刚刚从它的总公司德国拜耳摆脱出来,如今的科思创拥有大量的随意去调节本身的战略定位。目前为止,科思创在中国的项目投资已做到30亿英镑(等于34亿美金)。上年,科思创在产品研发层面的项目投资总共2.六亿英镑。 虽然中国的gdp增速已经变缓,但在2016年第一季度,科思创還是创出了13.3%的提高纪录。Thomas觉得那样大的一个经济大国,没法一直维持二位数的增速,是很一切正常的。 顺从本地市场要求 中国上海市的上海浦东新区,位于着科思创上海市研究所,有200名生物学家在里面工作中。管理中心的总体目标是为全世界市场出示科学研究和开发设计适用,而本地的市场喜好,则是自主创新的起始点。 四月,科思创在2016中国橡塑展上,展览了一套综合型诊疗设备。该设备可以对心率和心率开展同歩统计分析精确测量,且尺寸适合,可以置放在手拎包里。 提到这一产品,Thomas觉得十分自豪,他说道,这套设备特别适合中国乡村市场,本地高品质设备十分稀有,医生和护士常常必须一些便于带上的设备。 设备采用的生产工艺并不新奇,但科思创還是为他们找到适合的发展方向――将他们资金投入中国市场的新方法。 维持与顾客的密切联系,是科思创战略定位的关键基本方针之一,该企业觉得这一战略方针是尤为重要的,仅有那样,它的生物学家才可以和顾客一道寻找各种难题的解决方法。 携手并肩同濟 上海同济大学是科思创的长期性合作方之一,同濟为科思创研究所出示原材料及生产制造科学研究技术专业的优秀生优秀人才。研发部门也很愿意征募别的顶级高校的大学毕业生优秀人才。 除开它的风力设备和诊疗设备是专业对于中国的绿色发展和诊疗行业之外,Thomas表明她们还“关心中国的汽车制造业”。 本次橡塑展上,科思创展台上的职工还详细介绍了企业开发设计的纯电动车电池充电塔,具有耐温性且抗紫外光性,室外的使用期限也更长。 一旦中国逐渐规模性构建电池充电塔,这种产品将是科思创在中国的市场参与性的又一力证。 来源于:PUWORLD |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。