牌号简介 About |
---|
Ultem AM9085F长丝是以Ultem 9085树脂为原料生产的一种高性能聚醚酰亚胺共混产品。它有黑色和天然(未着色)颜色。它具有很高的耐热性和机械强度,在1.5和3.0 mm处符合UL94V-0标准(在UL IQ数据库中提供蓝卡),满足FAR 25.853和OSU 65/65标准,具有低毒性、烟雾和火焰演化。标称灯丝直径为1.79 mm±0.05 mm,线轴尺寸为1510 cc。 ULTEM™ AM9085F filament is a high performance polyetherimide blend product manufactured from ULTEM™ 9085 resin. It is available in black and natural (unpigmented) colors. It provides high heat resistance and mechanical strength, is UL94 V-0 compliant at 1.5 and 3.0 mm (Blue Cards are available on UL IQ Database), and meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. Nominal filament diameter is 1.79 mm ± 0.05 mm and it is available in a 1510 cc spool size. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
XY 方向 XY direction |
2180 | MPa | |
XZ 方向 XZ direction |
2560 | MPa | |
ZX 方向 ZX direction |
2440 | MPa | |
拉伸强度 tensile strength 2 |
|||
XY 方向,断裂 XY direction, fracture |
62.0 | MPa | |
XZ 方向,断裂 XZ direction, fracture |
80.0 | MPa | |
ZX 方向,断裂 ZX direction, fracture |
MPa | ||
拉伸应变 Tensile strain 2 |
|||
XY 方向,断裂 XY direction, fracture |
% | ||
XZ 方向,断裂 XZ direction, fracture |
% | ||
ZX 方向,断裂 ZX direction, fracture |
% | ||
弯曲模量 Bending modulus 3 |
|||
XY 方向 XY direction |
MPa | ||
XZ 方向 XZ direction |
MPa | ||
ZX 方向 ZX direction |
MPa | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 4 |
|||
XY 方向,23℃ XY direction, 23 ℃ |
J/m | ||
XZ 方向,23℃ XZ direction, 23 ℃ |
J/m | ||
ZX 方向,23℃ ZX direction, 23 ℃ |
J/m | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
ZX 方向:23℃ ZX direction: 23 ℃ |
J/m | ||
XY 方向:23℃ XY direction: 23 ℃ |
J/m | ||
XZ 方向:23℃ XZ direction: 23 ℃ |
J/m | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
XY 方向:1.8 MPa,未退火,3.20 mm XY direction: 1.8 MPa, unannealed, 3.20 mm |
℃ | ||
XZ 方向:1.8 MPa,未退火,3.20 mm XZ direction: 1.8 MPa, unannealed, 3.20 mm |
℃ | ||
ZX 方向:1.8 MPa,未退火,3.20 mm ZX direction: 1.8 MPa, unannealed, 3.20 mm |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:XY 方向 MD: XY direction |
1/℃ | ||
MD:XZ 方向 MD: XZ direction |
1/℃ | ||
MD:ZX 方向 MD: ZX direction |
1/℃ | ||
TD:XY 方向 TD: XY direction |
1/℃ | ||
TD:XZ 方向 TD: XZ direction |
1/℃ | ||
TD:ZX 方向 TD: ZX direction |
1/℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
XY 方向 XY direction |
ohms·cm | ||
XZ 方向 XZ direction |
ohms·cm | ||
介电常数 Dielectric constant |
|||
XY 方向:100 MHz XY direction: 100 MHz |
|||
XZ 方向:100 MHz XZ direction: 100 MHz |
|||
XZ 方向:500 MHz XZ direction: 500 MHz |
|||
XY 方向:500 MHz XY direction: 500 MHz |
|||
XZ 方向:1.00 GHz XZ direction: 1.00 GHz |
|||
XY 方向:1.00 GHz XY direction: 1.00 GHz |
|||
耗散因数 Dissipation factor |
|||
XZ 方向:100 MHz XZ direction: 100 MHz |
|||
XY 方向:100 MHz XY direction: 100 MHz |
|||
XZ 方向:500 MHz XZ direction: 500 MHz |
|||
XY 方向:500 MHz XY direction: 500 MHz |
|||
XZ 方向:1.00 GHz XZ direction: 1.00 GHz |
|||
XY 方向:1.00 GHz XY direction: 1.00 GHz |
|||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 5 |
|||
XY 方向,1.50 mm XY direction, 1.50 mm |
|||
XZ 方向,1.50 mm XZ direction, 1.50 mm |
|||
ZX 方向,1.50 mm ZX direction, 1.50 mm |
|||
XY 方向,3.00 mm XY direction, 3.00 mm |
|||
XZ 方向,3.00 mm XZ direction, 3.00 mm |
|||
ZX 方向,3.00 mm ZX direction, 3.00 mm |
|||
FAA Flammability(1.50 mm) FAA Flammability(1.50 mm) 6 |
FAR 25.853 | ||
OSU峰值放热速率(5 minute test,1.50 mm) OSU peak heat release rate (5 minute test, 1.50 mm) 6 |
kW/m² | FAR 25.853 | |
OSU总放热量(2 minute test,1.50 mm) OSU total heat release (2 minute test, 1.50 mm) 6 |
kW·min/m² | FAR 25.853 | |
垂直燃烧测试 Vertical combustion test |
|||
a,60s,passes at a,60s,passes at |
sec | ||
b,12s,passes at b,12s,passes at |
sec |
备注 |
---|
2. 类型 1, 5.0 mm/min |
3. 1.3 mm/min |
4. test coupons were printed using a Stratasys FORTUS† 900mc printer at high print density (88.5%) |
5. UL results provided herein may not be sufficient to waive end use part testing for UL listing. Contact UL for further details. |
6. XY Orientation |
【新闻资讯】查看全部
科莱恩色母粒的墨西哥工厂获ISO 22000认证
2021-03-21 搜料网资讯: 科莱恩的色母粒部门是颜料和功能性添加剂母料浓缩物和化合物的领先供应商。该部门日前宣布,其位于墨西哥城附近圣克拉拉科阿蒂特拉(Santa Clara Coatitla)的工厂已完成 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |