牌号简介 About |
---|
低密度湿固化聚乙烯化合物,用于低压建筑电线绝缘(CSA RW90、RWU90、AC90、TECK90-耐阳光)。聚氧化乙烯R/T-UV是一种低密度交联聚乙烯(XLPE)体系,可通过水分固化,由硅烷预接枝碱化合物A-3001和催化剂母料CAT-124组成。以适当的比例(80:20)混合和挤压,双组分混合物产生可通过暴露于70-95°C热水或甚至环境湿度固化的材料。根据CSA C22.2第38号规定,用pexidan r/t-uv制成的绝缘材料的额定温度为-40°C,并且可以在所有颜色和所有尺寸上标记为耐阳光(-sr)。根据C22.2 No.271,pexidan r/t-uv适用于CSA型RPV90和RPVU90光伏电线。环氧树脂R/T-UV不阻燃,无卤,符合RoHS标准。 Low density moisture curable polyethylene compound for low voltage building wire insulation (CSA RW90, RWU90, AC90, TECK90 - Sunlight Resistant). PEXIDAN ® R/T-UV is a low density XLPE system curable by moisture and consists of a silane pre-grafted base compound A-3001 and a catalyst masterbatch CAT-124. Mixed and extruded in the proper proportions (80:20), the two-component blend results in a material that is curable by exposure to 70-95°C hot water or even ambient moisture. Insulation made with PEXIDAN ® R/T-UV is rated to -40°C and may be marked Sunlight Resistant ("-SR") in all colors and in all sizes per CSA C22.2 No. 38. PEXIDAN ® R/T-UV is suitable for CSA Type RPV90 and RPVU90 photovoltaic wire per C22.2 No. 271. PEXIDAN ® R/T-UV is non-flame-retardant, halogen-free and RoHS-compliant. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
0.990 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.80 | g/10min | ASTM D1238 |
交叉结合的程度 The degree of cross combination |
70 | % | ASTM D2765 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂 fracture |
15.5 | MPa | CSA 22.2 No. 38 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
400 | % | CSA 22.2 No. 38 |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度的变化率 The rate of change in tensile strength |
|||
720 hr 720 hr 3 |
% | ||
121℃,168 hr 121℃,168 hr 4 |
% | ||
极限伸长率的变化率 Change rate of ultimate elongation |
|||
720 hr 720 hr 3 |
% | ||
121℃,168 hr 121℃,168 hr 4 |
% | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
变形 deformation |
% | CSA 22.2 No. 38 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相对电容率 Relative permittivity |
|||
60 Hz 60 Hz |
CSA 22.2 No. 38 | ||
绝缘电阻 insulation resistance |
|||
15℃ 15℃ |
Mohms/km | ||
after 12 weeks:90℃ after 12 weeks:90℃ |
Mohms/km | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
高温伸长率 High temperature elongation 5 |
|||
负荷下伸长率,150℃ Elongation under load, 150 ℃ 5 |
% | 内部方法 |
备注 |
---|
2. 23°C |
3. after xenon-arc exposure |
4. after thermal ageing |
5. 15 minutes, 0.2 N/mm² load |
【新闻资讯】查看全部
我国开发尼龙单体制备生物合成途径
2020-11-09 搜料网资讯: 10月20日,记者在采访湖北大学生命科学学院、省部共建生物催化与酶工程国家重点实验室李爱涛教授时了解到,李爱涛研究团队在尼龙单体制备领域取得重大突破,打破现 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |