牌号简介 About |
---|
Polycomp® CB 01/2 HSE是一种未填充的低流动聚丙烯共聚物化合物。它已开发用于要求良好的抗冲击性和长期接触沸水和乙二醇溶液稳定的塑件。 Polycomp CB 01/2 HSE is an unfilled low flow polypropylene copolymer compound. It has been developed for mouldings requiring good impact resistance and stabilized for long term contact with boiling water and glycol solutions. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.898 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
1.5 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD:3.0 mm MD:3.0 mm |
1.6 到 1.9 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3mm 3mm |
570 | J/m | ASTM D256 |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
3 mm 3 mm |
无断裂 | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,3.0 mm 0.45 MPa, unannealed, 3.0 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-30~30℃,3.00 mm MD:-30~30℃,3.00 mm |
1/℃ | ASTM D696 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,3.00 mm Shore D, 3.00 mm |
|||
邵氏 D,15 秒,3.00 mm Shore D, 15 seconds, 3.00 mm |
|||
洛氏硬度 Rockwell hardness |
|||
R 级,3.00 mm R-grade, 3.00 mm |
ASTM D785 | ||
拉伸强度 tensile strength 2 |
|||
3 mm 3 mm 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂,3 mm Fracture, 3 mm 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
3 mm 3 mm |
MPa | ASTM D790 |
备注 |
---|
2. 50 mm/min |
【新闻资讯】查看全部
EIA:预计美国可再生柴油供应将超过生物柴油
2022-03-31 据烃加工3月24日消息称,EIA 预计可再生柴油供应国内生产和净进口将在短期内超过生物柴油供应。EIA预计,可再生柴油供应量将在2022年增加到13万桶/天,在2050年增加到14.5万桶/天,这 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |