牌号简介 About |
---|
6.5%Gr PBT,UL94 V-0/5 V。 6.5% GR PBT, UL94 V-0/5V. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.44 | g/cm³ | ASTM D792 |
特定体积 Specific volume |
0.690 | cm³/g | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:1.5-3.2 mm MD:1.5-3.2 mm |
0.60 到 0.80 | % | |
MD:3.2-4.6 mm MD:3.2-4.6 mm |
0.80 到 1.0 | % | |
TD:1.5-3.2 mm TD:1.5-3.2 mm |
0.70 到 0.90 | % | |
TD:3.2-4.6 mm TD:3.2-4.6 mm |
% | ||
吸水率 Water absorption rate |
|||
24hr 24hr |
% | ASTM D570 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ||
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ||
球压测试 Ball pressure test |
|||
123~127℃ 123~127℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
|||
-40 到 40℃ -40 to 40 ℃ |
cm/cm/℃ | ||
60 到 138℃ 60 to 138 ℃ |
cm/cm/℃ | ||
相对温度指数 Relative temperature index |
℃ | UL 746 | |
电气性能 Electrical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
1.6 mm,在油中 1.6 mm in oil |
kV/mm | ||
3.2 mm,在空气中 3.2 mm in air |
kV/mm | ||
介电常数 Dielectric constant |
|||
100 Hz 100 Hz |
|||
1 MHz 1 MHz |
|||
耗散因数 Dissipation factor |
|||
100 Hz 100 Hz |
|||
1 MHz 1 MHz |
|||
耐电弧性 Arc resistance 5 |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) 6 |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
0.71 mm 0.71 mm |
|||
3.00 mm 3.00 mm |
|||
灼热丝可燃性指数 Glowing wire flammability index |
|||
1.0 mm 1.0 mm |
℃ | ||
3.0 mm 3.0 mm 7 |
℃ | ||
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
1 mm 1 mm |
℃ | ||
3 mm 3 mm |
℃ | ||
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength 3 |
|||
断裂 fracture 3 |
MPa | ASTM D638 | |
弯曲模量 Bending modulus 4 |
|||
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 4 |
|||
断裂,50 mm跨度 Fracture, 50 mm span 4 |
MPa | ASTM D790 |
备注 |
---|
3. 类型 1, 5.0 mm/min |
4. 1.3 mm/min |
5. 钨电极 |
6. Surface |
7. by VDE |
【新闻资讯】查看全部 ![]()
全球轮胎75“强”出炉
2021-09-07 搜料网资讯: 8月30日,由美国《轮胎商业》组织的2021年度全球轮胎75强排行榜公布。2020年,世界轮胎行业遭受新冠肺炎疫情冲击,轮胎销售额、利润、利润率等大幅下降,轮胎投资、研 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |