牌号简介 About |
---|
DAI-EL® G-8002是一种不透氧固化共聚物,设计用于挤出和注塑成型。DAI-EL® G-8002可与各种过氧化物固化系统一起配制,并可用于与其他弹性体共挤出。DAI-EL® G-8002具有优异的机械性能,具有很好的弯曲疲劳性能。与双酚固化氟弹性体相比,这种材料具有更好的抗蒸汽和水溶液性能。 DAI-EL® G-8002 is aperoxide curable copolymer designed for extrusion and injection molding. DAI-EL® G-8002 can be formulated with various peroxide cure systems and can be used for co-extrusion with other elastomers. DAI-EL® G-8002 provides superior mechanical properties, with very good flex fatigue behavior. In comparison to bisphenol cured fluoroelastomers, this material gives better resistance to steam and aqueous solutions. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.81 | g/cm³ | |
门尼粘度 Mooney viscosity |
|||
ML 1+10,121℃ ML 1+10,121℃ |
25 | MU | |
氟含量 Fluorine content |
66 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
66 | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
21.0 | MPa | |
100% 应变 100% strain |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ||
压缩形变 Compression deformation |
|||
200℃,70 hr 200℃,70 hr |
% | ASTM D395B | |
MH MH 2 |
lb·in | ||
ML ML 2 |
lb·in | ||
t'90(time to 90% cure) t'90(time to 90% cure) |
min | ||
ts2(焦化时间) Ts2 (coking time) |
sec | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
后固化时间 Post curing time |
|||
180℃ 180℃ |
hr | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time |
|||
Press Cure,160℃ Press Cure,160℃ |
min | ||
TR Test(TR10) TR Test(TR10) |
℃ | ASTM D1329 | |
|
备注 |
---|
2. MDR 2000 |
【新闻资讯】查看全部
2018「APFE」胶带世界,薄膜天下
2017-11-07 第十四届上海国际胶粘带、保护膜及光学膜展 第十四届上海国际功能薄膜、聚酯薄膜及技术展 展览时间: 2018年5月25-27日 展会地点: 国家会展中心(上海虹桥)6.1号馆 主办单位: 上 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |