牌号简介 About |
---|
TC-27 4A/B PrimoSoT 2是一种双组分水发泡软质聚氨酯泡沫系统。固化后的材料感觉类似于中等硬度的家具坐垫。bjb的6800系列颜料可以添加到b侧,以形成广泛的颜色。常见的应用有原型、假肢、医疗训练设备、电影特效道具等。这种材料通常是在柔韧的聚氨酯表皮材料(如BJB的Skinflex线或其他BJB弹性体)后面成型的。TC-274 A/B可以手动混合、机械分配或与快速混合机混合。 TC-274 A/B PolySoft 2 is a two-component water blown flexible polyurethane foam system. The cured material feels similar to a medium-firmness furniture cushion. BJB's 6800 Series Pigments may be added to the "B" side for developing a wide range of colors. Common applications are prototypes, prosthetics, medical training devices, movie special effects props and more. This material is frequently molded behind flexible polyurethane skin materials such as BJB's SkinFlex line or other BJB elastomers. TC-274 A/B can be hand mixed, machine dispensed, or mixed with a Jiffy Mixer®. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
Free rise Free rise |
g/cm³ | ||
-- -- 2 |
1.03 | g/cm³ | |
-- -- 3 |
1.19 | g/cm³ | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components |
|||
部件 A Component A |
按重量计算的混合比: 50, 按容量计算的混合比: 43 | ||
部件 B Component B |
按重量计算的混合比: 100, 按容量计算的混合比: 100 | ||
贮藏期限 Storage period |
26 | wk | |
热固性混合粘度 Thermosetting mixed viscosity |
|||
25℃ 25℃ 4 |
cP | ||
25℃ 25℃ 5 |
cP | ||
脱模时间 stripping time |
min | ||
Cream Time(25℃) Cream Time(25℃) |
sec | ||
Rise Time Rise Time |
min | ||
Tack Free Time Tack Free Time |
min |
备注 |
---|
2. Part B, 77°F |
3. Part A, 77°F |
4. Part A |
5. Part B |
【新闻资讯】查看全部
大型水泵叶轮使用三坐标停止测量
2016-03-30 在传统的大型水泵叶轮的加工制造过程中,加工量的确定是通过划线工人按进水口找圆,出水口找平来确定的。但是由于叶轮流道及前后盖板各表面均为铸造表面, 各表面的铸造余量十分不均匀,单凭划线工人用传统方法对叶轮进行划线操作,不仅要求工人有极高的经验,而且找出来的加工基准也十分粗糙,按此基准加工的叶 轮出现的偏差比较大,导致加工出来的叶轮与设计的理想尺寸相差甚远,以致在进行水力性能试验时达不到设计要求,而且由于叶轮水力中心线没在设计理论位置, 导致叶片的厚度不均匀,使机组振动噪音等各项要求严重超标。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |