牌号简介 About |
---|
30%玻璃增强,冲击改性热塑性合金。提高韧性和延展性。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
特定体积 Specific volume |
0.700 | cm³/g | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
250℃,5.0kg 250℃,5.0kg |
24 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
250℃,5 kg 250℃,5 kg |
12.0 | cm³/10min | |
265℃,5 kg 265℃,5 kg |
19.0 | cm³/10min | |
收缩率 Shrinkage rate |
|||
MD:0.75-2.3 mm MD:0.75-2.3 mm |
0.30 到 0.40 | % | |
MD:2.3-4.6 mm MD:2.3-4.6 mm |
% | ||
TD:0.75-2.3 mm TD:0.75-2.3 mm |
% | ||
TD:2.3-4.6 mm TD:2.3-4.6 mm |
% | ||
吸水率 Water absorption rate |
|||
24hr 24hr |
% | ASTM D570 | |
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 7 |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ 8 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 8 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23°C,Energy at Peak 23°C,Energy at Peak |
J | ||
23°C,Total Energy 23°C,Total Energy |
J | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,4.0 mm,64 mm跨距 1.8 MPa, unannealed, 4.0 mm, 64 mm span 8 |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 9 | |
-- -- |
℃ | ISO 306 | |
-- -- |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
流动:60~138℃ Flow: 60-138 ℃ |
1/℃ | ASTM E831 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:-40℃ TD:-40℃ |
1/℃ | ISO 11359-2 | |
RTI Elec RTI Elec |
°C | UL 746 | |
RTI Imp RTI Imp |
°C | UL 746 | |
RTI RTI |
°C | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
3.2 mm,在空气中 3.2 mm in air |
kV/mm | ASTM D149 | |
1.6 mm,在油中 1.6 mm in oil |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
|||
100 Hz 100 Hz |
|||
1 MHz 1 MHz |
|||
耗散因数 Dissipation factor |
|||
100 Hz 100 Hz |
|||
1 MHz 1 MHz |
|||
耐电弧性 Arc resistance 10 |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) 11 |
UL 746 | ||
高电压电弧起痕速率 (HVTR) High voltage arc marking rate (HVTR) |
UL 746 | ||
热丝引燃 (HWI) Hot wire ignition (HWI) |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
-- -- 2 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
抗张强度 Tensile strength |
|||
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/5 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
屈服 yield 3 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/5 | |
断裂 fracture 3 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus |
|||
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
-- -- 5 |
MPa | ISO 178 | |
弯曲应力 Bending stress |
|||
-- -- 5, 6 |
MPa | ISO 178 | |
屈服,50.0 mm 跨距 Yield, 50.0 mm span 4 |
MPa | ASTM D790 | |
断裂,50.0 mm 跨距 Fracture, 50.0 mm span 4 |
MPa | ASTM D790 |
备注 |
---|
2、5.0 mm/min |
3、类型 1, 5.0 mm/min |
4、1.3 mm/min |
5、2.0 mm/min |
6、at Yield |
7、80*10*3 sp=62mm |
8、80*10*4 mm |
9、速率 A (50°C/h), 载荷2 (50N) |
10、钨电极 |
11、Surface |
【新闻资讯】查看全部
伊士曼创新日聚焦创新型增长形式
2018-02-28 伊士曼化工公司近日举办了2018年度“创新日”活动,在活动中执行管理层探讨了公司当前对于创新的关注,以推动增长,创造价值。 伊士曼董事长兼首席执行官Mark Costa表示:“我们已构建起伊士曼独有的创新型高效增长模式,该模式涵盖了世界级技术平台,不断的市场开拓以及差异化的应用开发。其中,作为推动增长的关键因素,应用开发不仅展现了创新价值,还能够加速价值转化,同时有助于加深对于我们产品价值的认知。此外,通过积极高效的产品组合管理,公司的盈利以及现金流结构得以改善。得益于这些 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |