牌号简介 About |
---|
M710F(POK)是挤压级机械性能,属于发动机热塑性材料。该等级结合了高熔体强度和粘度,高耐化学性和阻隔性能。此外,该材料在室温和较低温度下均具有较高的抗冲击性,并具有良好的蠕变性能。M710F也能承受短期的高温暴露。M710F被设计用于要求挤出工艺。衬里、管道和吹膜应考虑这一等级的M710F,可在食品、药品、工业和消费家电市场上找到应用。 |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
抗拉强度 tensile strength |
|||
屈服 yield |
43 | MPa | ASTM D638 |
屈服 yield |
43 | MPa | ISO 527-1 |
拉伸模量 Tensile modulus |
|||
|
950 | MPa | ASTM D638 |
|
900 | MPa | ISO 527-1 |
弯曲强度 bending strength |
|||
|
40 | MPa | ASTM D790 |
|
MPa | ISO 178 | |
弯曲模量 Bending modulus |
|||
|
MPa | ASTM D790 | |
|
MPa | ISO 178 | |
邵氏硬度 Shore hardness |
|||
|
Shore D | ASTM D2240 | |
|
Shore D | ISO 868 | |
洛氏硬度 Rockwell hardness |
|||
|
R | ASTM D-785 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
伸长率 elongation |
|||
屈服拉伸 Yield tension |
% | ASTM D-638 | |
屈服拉伸 Yield tension |
% | ISO 527-1 | |
断裂拉伸 Breaking and stretching |
% | ASTM D-638 | |
断裂拉伸 Breaking and stretching |
% | ISO 527-1 | |
比重 proportion |
|||
|
g/cm³ | ASTM D792 | |
|
g/cm³ | ISO 1183 | |
吸水平衡 Water absorption balance |
|||
在50%RH下的 At 50% RH |
% | ASTM D570 | |
在50%RH下的 At 50% RH |
% | ISO 62 | |
吸水率 Water absorption rate |
|||
饱和时的 At saturation |
% | ASTM D570 | |
饱和时的 At saturation |
% | ISO 62 | |
熔融指数 Melt index |
|||
|
g/10min | ASTM D1238 | |
|
ml/10min | ISO 1133 | |
模具收缩率 Mold shrinkage rate |
|||
MD,3mm MD,3mm |
% | ASTM D-955 | |
TD,3mm TD,3mm |
% | ASTM D-955 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
未划痕的 Unscratched |
ISO 179/1eU | ||
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
kJ/m² | ISO 179/1eA | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
未划痕的 Unscratched |
ASTM D256 | ||
未划痕的 Unscratched |
ISO 180/1U | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
J/m | ASTM D256 | |
|
KJ/m² | ISO 180/1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体温度 Melt Temperature |
|||
|
℃ | ASTM D3418 | |
|
℃ | ISO 11357 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
25℃-55℃,TD 25℃-55℃,TD |
ASTM E831 | ||
25℃-55℃,MD 25℃-55℃,MD |
ASTM E831 | ||
维卡软化温度 Vicat Softening Temp |
|||
5kg 5kg |
℃ | ASTM D1525 | |
50N 50N |
℃ | ISO 306/B50 | |
热变形温度 Hot deformation temperature |
|||
66psi 66psi |
℃ | ASTM D648 | |
264psi 264psi |
℃ | ASTM D648 | |
0.4MPa 0.4MPa |
℃ | ISO 75 | |
1.8MPa 1.8MPa |
℃ | ISO 75 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength |
|||
短期3mm Short term 3mm |
kV/mm | ASTM D149 | |
短期2mm Short term 2mm |
kV/mm | ASTM D149 | |
体积电阻率 Volume resistivity |
|||
|
ohm·cm | ASTM D257 | |
表面电阻率 Surface resistivity |
|||
|
ohm/sq. | ASTM D257 | |
介电常数 Dielectric constant |
|||
60Hz时 At 60Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
60Hz时 At 60Hz |
ASTM D150 |
备注 |
---|
设定温度:推荐熔化温度:210-230C(410-446℉)。不得超过265摄氏度(509℉)。在温度范围的高端停留时间较长,可能会导致热降解和物理性质的损失。保持较低的熔体温度,以提高熔体质量(<210C)。 启动和清洁指南:首先启动净化聚合物(LDPE、PP、HDPE、PETG),并逐渐转变为丙酮。如果您关闭机器超过0.5小时,请使用清洗机清洗袋酮聚合物生产出丙酮产品后,请立即彻底清洗桶。其他的同时也有商业净化化合物。 干燥:建议在80℃下干燥约3~4小时。酮应该干燥通过烤箱或料斗干燥器,以防止表面问题,如银条纹,流口水或空洞。如果干燥温度过高或干燥时间太长,就会导致球团变色。 |
【新闻资讯】查看全部
伊之密参展KUTENO 2022
2022-05-12 德国当地时间5月10日,为期三天的KUTENO 2022在德国雷达-维登布吕克如期举行,伊之密(德国子公司)携FF电动注塑机及整体解决方案亮相展会。 在伊之密展位上,不仅摆放了款式多样的塑料制 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |