牌号简介 About |
---|
用于薄膜产品的低密度聚乙烯离聚物的优点和特点M21E730是一种由乙烯-甲基丙烯酸(MAA)共聚物中和而成的离聚物。它具有以下特性:极高的冲击强度、优异的下拉性能、极低的抗撕裂性、在机器和横向上的传播性能、良好的光学性能、M21E730已被开发用于易撕膜应用,如整理收缩膜、信封、外包装和袋子。它可以与其他类型的聚乙烯混合或共挤,以定制性能。 LDPE ionomer for film products Benefits & Features M21E730 is an ionomer, produced by the neutralization of an ethylene methacrylic acid (MAA) copolymer. It offers the following properties: Very high impact strength Exceptional drawdown Very low resistance to tear propagation in both machine and transverse directions Good optical properties Applications M21E730 has been developed for easy tear film applications such as collation shrink film, envelopes, overwrap and bags. It can be blended or co-extruded with other types of polyethylene to tailor performance. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.933 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.50 | g/10min | ISO 1133 |
Methacrylic Acid Content Methacrylic Acid Content |
1.7 | % | Internal Method |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
50 | µm | |
拉伸模量 Tensile modulus |
ISO 1184 | ||
1% 正割,MD,50 µm,吹塑薄膜 1% secant, MD, 50 µ m, blow molded film |
165 | MPa | ISO 1184 |
1% 正割,TD,50 µm,吹塑薄膜 1% secant, TD, 50 µ m, blow molded film |
MPa | ISO 1184 | |
拉伸强度 tensile strength |
ISO 1184 | ||
MD,屈服,50 µm,吹塑薄膜 MD, yield, 50 µ m, blow molded film |
MPa | ISO 1184 | |
TD,屈服,50 µm,吹塑薄膜 TD, yield, 50 µ m, blow molded film |
MPa | ISO 1184 | |
拉伸强度 tensile strength |
ISO 1184 | ||
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ISO 1184 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ISO 1184 | |
拉伸应变 Tensile strain |
ISO 1184 | ||
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ISO 1184 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ISO 1184 | |
落锤冲击 Drop hammer impact |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film |
g | ASTM D1709-A | |
撕裂强度 tear strength |
|||
TD,50 µm,吹塑薄膜 TD, 50 µ m, blow molded film |
g | ASTM D1922 | |
MD,50 µm,吹塑薄膜 MD, 50 µ m, blow molded film |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,50.0 µm,吹塑薄膜 45 °, 50.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
微塑料确实存在于人类体内的循环系统中
2022-04-11 由生态毒理学家Heather Leslie和分析化学家Marja Lamoree领导的研究小组首次表明,来自我们生活环境的微塑料也存在于人类的循环系统中。这项名为Immunoplast的研究项目的结果于3月出现在科 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |