牌号简介 About |
---|
AOC的VipelF707-PVA系列是间苯二甲酸NPG,两级,不饱和聚酯树脂。浸湿、固化和搬运特性是通用树脂的典型特征。使用Vipel F707-PVA树脂将PVC粘合层与PVC粘合。用途广泛,适用于手工制作、喷涂、纤维缠绕等多种制造方法。 AOC's Vipel F707-PVA series are isophthalic-NPG, two stage, unsaturated polyester resins. The wet-out, cure and handling characterisitcs are typical of general purpose resins. BENEFITS PVC Bonding Laminates made with Vipel F707-PVA resin bond to PVC. Versatile Suitable for various fabricating methods such as hand lay-up, spray-up and filament winding. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
苯乙烯含量 styrene content |
48 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
3860 | MPa | ASTM D638 |
拉伸强度 tensile strength |
86.2 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
3.7 | % | ASTM D638 |
弯曲模量 Bending modulus |
4070 | MPa | ASTM D790 |
弯曲强度 bending strength |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Gel to Peak Gel to Peak |
min | ||
放热峰值 exothermic peak |
℃ | ||
触变指数 Thixotropic index |
|||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ||
粘度 viscosity |
|||
布络克菲尔德 LV Brookfield LV |
Pa·s | ||
胶凝时间 Gelation time |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
巴斯夫重申宏伟的气候保护目标,并采取措施减少产品碳足迹
2022-04-01 ●2030 年二氧化碳排放量将较 2018 年减少 25%,到 20501 年实现全球二氧化碳净零排放 ●到 2030 年,巴斯夫2021 全球电力需求的总量将 100% 来自可再生能源 ●巴斯夫准备向客户提供首批净 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |