牌号简介 About |
---|
透明、标准流量聚醚酰亚胺 |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 Tensile Stress Tensile Strength |
|||
屈服 yld,类型I Type I,5 mm/min Yield yld, Type I, Type I, 5 mm/min |
110 | MPa | ASTM D638 |
断裂 brk ,类型I Type I,5 mm/min Broken BRK, Type I, Type I, 5 mm/min |
90 | MPa | ASTM D638 |
屈服 yld,50 mm/min Yield yld, 50 mm/min |
105 | MPa | ISO 527-2 |
断裂 brk,50 mm/min Broken BRK, 50 mm/min |
85 | MPa | ISO 527-2 |
拉伸应变 Tensile Strain Tensile Strain |
|||
屈服 yld,类型I Type I,5 mm/min Yield yld, Type I, Type I, 5 mm/min |
7 | % | ASTM D638 |
断裂 brk,类型I Type I,5 mm/min Broken BRK, Type I, Type I, 5 mm/min |
% | ASTM D638 | |
屈服 yld,5 mm/min Yield yld, 5 mm/min |
% | ISO 527-2 | |
断裂 brk,5 mm/min Broken BRK, 5 mm/min |
% | ISO 527-2 | |
拉伸模量 Tensile Modulus Tensile Modulus |
|||
5 mm/min 5 mm/min |
MPa | ASTM D638 | |
1 mm/min 1 mm/min |
MPa | ISO 527-2 | |
弯曲强度 Flexural Stress, Flexural Strength, |
|||
屈服, 1.3 mm/min, 50 mm span |
MPa | ASTM D790 | |
屈服, 2.6 mm/min, 100 mm span |
MPa | ASTM D790 | |
屈服, 2 mm/min Yield, 2 mm/min |
MPa | ISO 178 | |
弯曲模量 Flexural Modulus Flexural Modulus |
|||
1.3 mm/min, 50 mm span 1.3 mm/min, 50 mm span |
MPa | ASTM D790 | |
2.6 mm/min, 100 mm span 2.6 mm/min, 100 mm span |
MPa | ASTM D790 | |
2 mm/min 2 mm/min |
MPa | ISO 178 | |
泰伯耐磨性 Taber Abrasion Taber Abrasion |
|||
CS-17, 1 kg CS-17, 1 kg |
mg/1000cy | SABIC method | |
球压硬度 Ball Indentation Hardness Ball indentation hardness |
|||
H358/30 H358/30 |
MPa | ISO 2039-1 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁无缺口冲击强度 Izod unnotched Impact Strength Izod unnoticed Impact Strength of Cantilever Beam |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
80*10*4 +23°C 80*10*4 +23°C |
KJ/m² | ISO 180/1U | |
80*10*4 -30°C 80*10*4 -30°C |
KJ/m² | ISO 180/1U | |
悬臂梁缺口冲击强度 Izod notched Impact Strength Izod notched Impact Strength |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ |
J/m | ASTM D256 | |
反向缺口 Reverse Notched,3.2 mm Reverse Notched, 3.2 mm |
J/m | ASTM D256 | |
80*10*4 +23°C 80*10*4 +23°C |
KJ/m² | ISO 180/1A | |
80*10*4 -30°C 80*10*4 -30°C |
KJ/m² | ISO 180/1A | |
Gardner Gardner |
|||
23℃ 23℃ |
J | ASTM D3029 | |
装有测量仪表的落镖冲击 Instrumented Dart Impact Total Energy Instrumented Dart Impact Total Energy with measuring instruments |
|||
23℃ 23℃ |
J | ASTM D3763 | |
简支梁缺口冲击强度 Charpy notched Impact Strength Charpy Notched Impact Strength |
|||
V型缺口 V-notch,23℃, 80*10*4 sp=62mm V-notch, 23 ℃, 80 * 10 * 4 sp=62mm |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/2C | |
V型缺口 V-notch,-30℃, 80*10*4 sp=62mm V-notch, -30 ℃, 80 * 10 * 4 sp=62mm |
kJ/m² | ISO 179/1eA | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp. Vicat Softening Temperature |
|||
B/50 B/50 |
℃ | ASTM D1525 | |
A/50 A/50 |
℃ | ISO 306/B | |
B/50 B/50 |
℃ | ISO 306/B | |
B/120 B/120 |
℃ | ISO 306/B | |
热变形温度 HDT |
|||
1.82 MPa, 3.2mm,未退火 unannealed |
℃ | ASTM D648 | |
0.45MPa,120*10*4 sp=100mm 0.45MPa,120*10*4 sp=100mm |
℃ | ISO 75/Be | |
1.8 MPa,120*10*4 sp=100mm 1.8 MPa,120*10*4 sp=100mm |
℃ | ISO 75/Ae | |
线性热膨胀系数 CTE Linear coefficient of thermal expansion CTE |
|||
-20°C to 150°C,流动 flow |
1/℃ | ASTM E831 | |
-20°C to 150°C,横向 xflow |
1/℃ | ASTM E831 | |
23°C to 150°C,流动 flow |
1/℃ | ISO 11359-2 | |
23°C to 150°C,横向 xflow |
1/℃ | ISO 11359-2 | |
导热系数 Thermal Conductivity Thermal conductivity |
|||
|
W/m-°C | ASTM C177 | |
|
W/m-°C | ISO 8302 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
比重 Specific Gravity Specific Gravity |
ASTM D792 | ||
吸水率 Water Absorption Water Absorption |
|||
23°C/24hrs 23°C/24hrs |
% | ASTM D570 | |
23°C/饱和 Saturated 23 ° C/Saturated |
% | ASTM D570 | |
23°C/饱和 Saturated 23 ° C/Saturated |
% | ISO 62 | |
23°C / 50% RH 23°C / 50% RH |
% | ISO 62 | |
成型收缩率 Mold Shrinkage Mold Shrinkage |
|||
在栏杆上 on Tensile Bar,流动 flow On Tensile Bar on railing, flowing flow |
% | SABIC method | |
流动 flow,3.2 mm Flow, 3.2 mm |
% | SABIC method | |
熔体质量流动速率 Melt Flow Rate Melt Flow Rate |
|||
337°C/6.6 kgf 337°C/6.6 kgf |
g/10min | ASTM D1238 | |
泊松比 Poisson's Ratio |
ASTM E132 | ||
密度 Density Density |
g/cm³ | ISO 1183 | |
熔体体积流动速率 Melt Volume Rate Melt Volume Rate |
|||
360°C/5.0 kg 360°C/5.0 kg |
cm³/10min | ISO 1133 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume Resistivity |
|||
|
ohm·cm | ASTM D257 | |
|
ohm·cm | IEC 60093 | |
介电强度 Dielectric Strength Dielectric Strength |
|||
空气 air,1.6 mm Air, 1.6 mm |
kV/mm | ASTM D149 | |
油中 oil,1.6 mm Oil in oil, 1.6 mm |
kV/mm | ASTM D149 | |
油中 oil,3.2 mm Oil in oil, 3.2 mm |
kV/mm | ASTM D149 | |
油中 oil,0.8 mm Oil in oil, 0.8 mm |
kV/mm | IEC 60243-1 | |
油中 oil,1.6 mm Oil in oil, 1.6 mm |
kV/mm | IEC 60243-1 | |
油中 oil,3.2 mm Oil in oil, 3.2 mm |
kV/mm | IEC 60243-1 | |
介电常数 Relative Permittivity Relative permittivity |
|||
100 Hz 100 Hz |
ASTM D150 | ||
1 kHz 1 kHz |
ASTM D150 | ||
1 MHz 1 MHz |
IEC 60250 | ||
50/60 Hz 50/60 Hz |
IEC 60250 | ||
耗散因数 Dissipation Factor Dissipation Factor |
|||
100 Hz 100 Hz |
ASTM D150 | ||
1 KHz 1 KHz |
ASTM D150 | ||
2450 MHz 2450 MHz |
ASTM D150 | ||
50/60 Hz 50/60 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
2450 MHz 2450 MHz |
IEC 60250 | ||
表面电阻率 Surface Resistivity Surface Resistivity |
ohm | IEC 60093 | |
相比漏电起痕指数 Comparative Tracking Index Compared Tracking Index |
|||
|
V | IEC 60112 | |
M M |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
灼热丝可燃性指数 Glow Wire Flammability Index Glow Wire Flammability Index |
|||
960°C 960°C |
mm | IEC 60695-2-12 | |
极限氧指数 Oxygen Index Oxygen Index |
% | ISO 4589-2 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
供需压力改善,化工原料PX完成7连涨
2017-11-10 10月27日至11月7日,亚洲化工原料PX价格实现7连涨,累计上涨了61.5美元/吨,目前已经成功突破900美元/吨CFR中国关口。成本端原油在超供格局好转预期下强势攀升、中国PTA工厂需求目前已经开始缓慢复苏,而消息面利好因素也在逐渐增多,市场整体气氛趋于向暖,也在进一步助推了PX价格走势上扬。 成本端油市利多氛围较为明显:其一,因为地缘冲突因素加剧了市场担忧气氛,沙 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |