牌号简介 About |
---|
Solef®11008/0003 PVDF是一种低粘度柔性PVDF共聚物树脂,通常通过挤出或注射成型进行加工。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
比重 Specific Gravity Specific Gravity |
1.75-1.80 | ASTM D792 | |
熔体质量流动速率 Melt Flow Rate Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
5.5-11 | g/10min | ASTM D1238 |
吸水率 Water Absorption Water Absorption |
|||
24hr,23℃ 24hr,23℃ |
<0.040 | % | ASTM D570 |
模具收缩率 Mold Shrinkage Mold Shrinkage |
2.00-3.00 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile Modulus Tensile Modulus |
|||
23℃,2.0 mm 23℃,2.0 mm |
800-1200 | MPa | ASTM D638 |
拉伸强度 Tensile Strength Tensile Strength |
|||
屈服 yld,23℃,2.00 mm Yield yld, 23 ℃, 2.00 mm |
MPa | ASTM D638 | |
断裂 brk,23℃,2.00 mm Broken BRK, 23 ℃, 2.00 mm |
MPa | ASTM D638 | |
拉伸伸长率 Tensile Elongation Tensile Elongation |
|||
屈服 yld,23℃,2.00 mm Yield yld, 23 ℃, 2.00 mm |
% | ASTM D638 | |
断裂 brk,23℃,2.00 mm Broken BRK, 23 ℃, 2.00 mm |
% | ASTM D638 | |
泰伯耐磨性 Taber Abrasion Taber Abrasion |
|||
1000次循环,1000 g,CS-10车轮 1000 cycles, 1000 g, CS-10 wheels |
mg | ASTM D4060 | |
摩擦系数 Frictional coefficient Frictional coefficient |
|||
动态 Dynamic Dynamic |
ASTM D1894 | ||
静态 Static Static |
ASTM D1894 | ||
硬度计硬度 Durometer Hardness |
ASTM D2240 | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
|||
23℃,4.00 mm 23℃,4.00 mm |
J/m | ASTM D6110 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass Transition Temperature Glass Transition Temperature |
℃ | ASTM D4065 | |
维卡软化温度 Vicat Softening Temperature Vicat Softening Temperature |
℃ | ASTM D1525 | |
熔融温度 Melting temperature Melting temperature |
℃ | ASTM D3418 | |
峰值结晶温度(DSC) Peak Crystallization Temperature (DSC) Peak Crystallization Temperature (DSC) |
℃ | ASTM D3418 | |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
流动 flow,0-40℃ Flow, 0-40 ℃ |
cm/cm/℃ | ASTM D696 | |
比热 Specific Heat Specific Heat |
|||
23℃ 23℃ |
J/kg/℃ | ASTM E968 | |
100℃ 100℃ |
J/kg/℃ | ASTM E968 | |
导热系数 Thermal Conductivity Thermal conductivity |
W/m/K | ASTM C177 | |
结晶热 Crystallization Heat Crystallization Heat |
J/g | ASTM D3417 | |
熔化热 Heat of Fusion Heat of Fusion |
J/g | ASTM D3417 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface Resistivity Surface Resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume Resistivity Volume Resistance |
ohms·cm | ASTM D257 | |
介电强度 Dielectric Strength Dielectric Strength |
|||
23℃,1 mm 23℃,1 mm |
kV/mm | ASTM D149 | |
介电常数 Dielectric Constant Dielectric Constant |
|||
23℃,1 MHz 23℃,1 MHz |
ASTM D150 | ||
耗散因数 Dissipation Factor Dissipation Factor |
|||
23℃,1 MHz 23℃,1 MHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating Flame Class Rating |
|||
0.1 mm 0.1 mm |
UL 94 | ||
极限氧指数 Oxygen Index Oxygen Index |
|||
3.00 mm 3.00 mm |
% | ASTM D2863 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
美国塑料公约要求淘汰11种产品和材料
2022-01-26 搜料网资讯: 美国塑料公约近期公布了问题和不必要的材料清单,确定11制造商产品和资料,其中列出了11种与包装有关的产品和材料,这些产品和材料目前在美国不能大规模地被重复使 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |