牌号简介 About |
---|
Ultramid®STAR S 60X1 V30 Grey R7035 CF是一种基于非卤化阻燃体系和专利高流动性聚酰胺6树脂的牌号,该树脂由30%的玻璃纤维增强,热稳定,用于注塑成型。该级别是热稳定的,并提供优化的注塑性能。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
吸水率 Water Absorption Water Absorption |
|||
24h,23℃ 24h,23℃ |
0.9 | % | ISO 62 |
平衡 equilibrium,23℃ Equilibrium equilibrium, 23 ℃ |
4.1 | % | ISO 62 |
吸湿性 Moisture Absorption Moisture Absorption |
|||
平衡 equilibrium,23℃,50% r.h. Equilibrium equilibrium, 23 ℃, 50% r. h |
1.7 | % | ISO 62 |
密度 Density Density |
1420 | kg/m³ | ISO 1183 |
成型收缩率 Molding Shrinkage Molding shrinkage |
|||
平行 parallel Parallel |
0.25 | % | ISO 294-4 |
法向 normal Normal |
% | ISO 294-4 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile Modulus Tensile Modulus |
|||
干燥 dry Dry |
MPa | ISO 527 | |
湿润 cond. Wet Cond |
MPa | ISO 527 | |
拉伸强度 Tensile Strength Tensile Strength |
|||
断裂 brk,干燥 dry Broken BRK, dry dry |
MPa | ISO 527-2 | |
断裂 brk,湿润 cond. Broken BRK, wet Cond |
MPa | ISO 527-2 | |
断裂 brk,干燥 dry Broken BRK, dry dry |
MPa | ISO 527-2 | |
拉伸应变 Tensile Strain Tensile Strain |
|||
断裂 brk,干燥 dry Broken BRK, dry dry |
% | ISO 527 | |
断裂 brk,湿润 cond. Broken BRK, wet Cond |
% | ISO 527 | |
断裂伸长率 Elongation at Break Elongation at Break |
% | ASTM D638 | |
弯曲模量 Flexural Modulus Flexural Modulus |
|||
干燥 dry Dry |
MPa | ISO 178 | |
湿润 cond. Wet Cond |
MPa | ISO 178 | |
干燥 dry Dry |
MPa | ASTM D790 | |
弯曲强度 Flexural Strength Flexural Strength |
|||
干燥 dry Dry |
MPa | ISO 178 | |
湿润 cond. Wet Cond |
MPa | ISO 178 | |
干燥 dry Dry |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
|||
-30 ℃,干燥 dry -30 ℃, dry |
kJ/m² | ISO 179/1eA | |
23℃,干燥 dry 23 ℃, dry |
kJ/m² | ISO 179/1eA | |
23℃,湿润 cond. 23 ℃, moist cond |
|||
简支梁无缺口冲击强度 Charpy Unnotched Impact strength Charpy Unnotch Impact strength |
|||
-30 ℃,干燥 dry -30 ℃, dry |
kJ/m² | ISO 179/1eU | |
23℃,干燥 dry 23 ℃, dry |
kJ/m² | ISO 179/1eU | |
23℃,湿润 cond. 23 ℃, moist cond |
|||
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
|||
23℃,干燥 dry 23 ℃, dry |
KJ/m² | ISO 180/1A | |
23℃,湿润 cond. 23 ℃, moist cond |
KJ/m² | ISO 180/1A | |
23℃,干燥 dry 23 ℃, dry |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Izod Unnotched Impact strength Izod Unnotched Impact strength of cantilever beam |
|||
23℃,干燥 dry 23 ℃, dry |
KJ/m² | ISO 180/1U | |
23℃,湿润 cond. 23 ℃, moist cond |
KJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
0.45 MPa 0.45 MPa |
℃ | ISO 75-1/-2 | |
1.80 MPa 1.80 MPa |
℃ | ISO 75-1/-2 | |
熔融温度 Melting temperature Melting temperature |
℃ | ISO 11357-3 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface Resistivity Surface Resistivity |
ohm | IEC 62631-3-2 | |
体积电阻率 Volume Resistivity Volume Resistance |
ohm·m | IEC 62631-3-1 | |
耐电强度 Electric strength Electric strength |
|||
干燥 dry,d=0.8 mm Dry, d=0.8 mm |
kV/mm | IEC 60243-1 | |
湿润 cond.,d=2.0 mm Wet Cond, D=2.0 mm |
kV/mm | IEC 60243-1 | |
干燥 dry,d=2.0 mm Dry, d=2.0 mm |
kV/mm | IEC 60243-1 | |
相对电容率 Relative Permittivity Relative permittivity |
|||
干燥 dry Dry |
IEC 62631-2-1 | ||
湿润 cond. Wet Cond |
IEC 62631-2-1 | ||
相比漏电起痕指数 Comparative Tracking Index Compared Tracking Index |
|||
干燥 dry Dry |
IEC 60112 | ||
湿润 cond. Wet Cond |
IEC 60112 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating Flame Class Rating |
|||
1.6 mm 1.6 mm |
calss | IEC 60695-11-10 | |
0.8 mm 0.8 mm |
calss | IEC 60695-11-10 | |
3.2 mm 3.2 mm |
calss | IEC 60695-11-10 | |
灼热丝可燃性指数 Glow Wire Flammability Index(GWFI) Glow Wire Flammability Index (GWFI) |
|||
0.8 mm 0.8 mm |
℃ | IEC 60695-2-12 | |
1.6 mm 1.6 mm |
℃ | IEC 60695-2-12 | |
3.2 mm 3.2 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Glow Wire Ignitability Temperature(GWIT) Glow Wire Ignitability Temperature (GWIT) |
|||
0.8 mm 0.8 mm |
℃ | IEC 60695-2-13 | |
1.6 mm 1.6 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Oxygen Index Oxygen Index |
% | ISO 4589-2 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
助剂企业大幅涨价 上调幅度达10%
2017-03-07 重要链接:今年还是中国的峰会大年,实体行业需要接连面对3月份开“两会”,5月份要开“一带一路”峰会,9月份的金砖国家峰会,以及近几年约定俗成的第四季度雾霾大会。这也导致国内环保压力急剧增大,并且影响到各种原料的上涨! 据悉,第十二届全国人民代表大会第五次会议和政协第十二届全国委员会第五次会议,将分别于2017年3月5日和3月3日在北京召开。为确保“两会”在此期间能够拥有蓝天白云,防止高污染,京津冀相关政府紧急布局,有多家媒体报道当地部分化工企业已经收到2月下旬至3月上旬的环 |
助剂企业大幅涨价 上调幅度达10% 关键连接:2020年還是我国的高峰会大年夜,实体行业必须连续应对3月份开“全国两会”,5月份要开“一带一路”高峰会,9月份的金砖五国高峰会,及其近些年约定成俗的第四季度雾霾天气交流会。这也造成 中国环境保护工作压力大幅度扩大,而且危害到各种各样原料的增涨! 据了解,第十二届全国代表大会第五次大会和市政协第十二届全国各地联合会第五次大会,将各自于2017年3月5日和3月3日北京举办。为保证“全国两会”在这段时间可以有着蓝天白云草地,避免高耗能,京津冀一体化有关政府部门应急合理布局,有好几家新闻媒体本地一部分化工厂企业早已接到2月中下旬至3月下旬的环境保护减产命令,一些高耗能企业将被停业整顿。导致原料供给量降低,进而促进一些原料产品报价升高。 在二月中下旬,由环保部部长陈吉宁及此外四位部长亲自领队的稽查组也已逐渐入驻河北省等七省份进行历时一个月的重点监督,在这段时间环境保护部将赴北京市、天津市、河北省、山西省、山东省、河南省等相关省(市)进行年度第一季度空气指数重点监督。环境保护部已经执行至今最强有力的室内空气治理行動,也是继去年年底掀起的“环境保护飓风”后又一对策。本次环保督查停业整顿重环境污染企业,意料可能导致供货降低,促进原料等涨价。 融合之上的见解,化工产品市场可能仍然高溫运作,现有一部分代理商逐渐压货。2017年,伴随着环境因素、现行政策要素、环境保护工作压力的危害,化工厂市场可否经得住市场的重重的磨练,是每一个化工厂企业所思索的不容乐观难题。 3月化工厂、改性剂、原料贯彻落实涨价: 市场再度涨价通告,而且是涨价富有很难买到原料。 不必谈价钱,你的经销商货源充足让你,便是较大 的成功了! 3月纺织品原料贯彻落实涨价: 纺织品老总说:“假如坯布不涨价得话,大家只有喝西北风来到”。而今日,原料企业公布氨纶涨价通告。一波接一波的涨价公示,令人压抑感的揣但是气。 前不久,化学纤维商品行情揠苗助长,聚脂涤纶布受原料行情危害,最近企业价格有一定的下降,一部分特惠扩张。殊不知,氨纶市场确是瘋狂重现,“股票追涨3000”、“价格当日合理”、“不订购”…相近涨价信息内容再度走红网络! 股票追涨3000、价格当日合理、不接纳订购... 至上年第三季度至今,中下游纺织市场形势度逐渐回暖,大部分企业很多年的坯布库存量得到清除,在库存量清除的另外,市场接单子状况也出現明显改善,因此引起了对化学纤维原料的购置潮。而现如今三月份的传统式纺织热季也早已来临,面料市场订单信息的转好亦推动原料市场的要求。 另一方面,自上年至今,弹性类面料出現了热卖,也是在去年末迈入了要求高峰期,据市场掌握,江浙地区圆机启动负载正逐渐回暖,现阶段在5-6成,而包纱总体负载在7成上下水准,而一部分纺织企业体现弹性面料的订单信息早已收到了4月末,对氨纶商品的购置潮也促使氨纶企业的原料库存量得到维持底位,亦给氨纶企业涨价姿势以支撑点。 来源于:微众圈 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。
电邮一份说明书
PDF文档名:搜料网-Ultramid® STAR S 60X1 V30 GREY R7035 CF证书
发送至:(多个地址,中间以逗号隔开)
发送一份副本给我:您还没有填写邮箱!(点击完善资料)