牌号简介 About |
---|
本产品为热稳定型无卤阻燃PA66,在0.4mm的时候可以达到UL94 V0,在室外使用场景,具备一定的抗UV耐候效果。该材料不含玻纤碳纤等增强物,可广泛应用于电子电器、家电及汽车电子等领域。This product is a heat stable halogen-free flame retardant PA66, which can reach UL94 V0 at 0.4mm. It has a certain UV and weather resistance effect in outdoor use scenarios. This material does not contain reinforcing materials such as glass fiber and carbon fiber, and can be widely used in fields such as electronics, home appliances, and automotive electronics. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
1.16 | g/cm³ | ISO 1183/A |
成型收缩率 Molding Shrinkage Molding shrinkage |
|||
TD TD |
1.3 | % | ISO 294-4 |
MD MD |
1.5 | % | ISO 294-4 |
吸水率 Water Absorption Water Absorption |
|||
23℃,24hr 23℃,24hr |
0.88 | % | ISO 62 |
平衡 equilibrium,23℃ Equilibrium equilibrium, 23 ℃ |
2.7 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile Modulus Tensile Modulus |
MPa | ISO 527-2/1A | |
拉伸强度 Tensile Strength Tensile Strength |
|||
屈服 yld Yield yld |
MPa | ISO 527-2/1A | |
断裂 brk Broken BRK |
MPa | ISO 527-2/1A | |
拉伸应变 Tensile Strain Tensile Strain |
|||
断裂 brk Broken BRK |
% | ISO 527-2 | |
弯曲模量 Flexural Modulus Flexural Modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 Flexural Strength Flexural Strength |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength Charpy Unnotch Impact strength |
|||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
0.45 MPa,未退火 unannealed 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
1.8 MPa,未退火 unannealed 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
熔融温度 Melting temperature Melting temperature |
℃ | ISO 11357-3 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface Resistivity Surface Resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume Resistivity Volume Resistance |
ohms·cm | IEC 60093 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部 ![]()
十三个成绩为你片面解析黑色母粒
2018-03-01 在塑料制品成型加工中,黑色母粒几乎人人都用过,用于染色,防老化,导电制品等等。但在使用过程中常常会出现各种问题,困扰我们。今天小编就将大家共同关心的一些问题进行探讨,希望能给您带来收获。 1.黑色母粒的组成? 组成黑色母粒的材料有: |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |