牌号简介 About |
---|
SCLAIR® 14G是一种中密度聚乙烯材料,。 该产品在北美洲有供货,加工方式为:薄膜挤出。 SCLAIR® 14G的主要特性有: 丁烯共聚单体 加工性能良好 加工助剂 抗氧化剂 可接触食品 典型应用领域包括: 电影 食品接触应用 SCLAIR® 14G is a Medium Density Polyethylene material. It is available in North America for film extrusion. Important attributes of SCLAIR® 14G are: Antioxidant Butene Comonomer Food Contact Acceptable Good Processability Processing Aid Typical applications include: Film Food Contact Applications |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.936 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.72 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
吹塑薄膜 Blown film |
0.24 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
38 | µm | |
割线模量 Secant modulus |
|||
1% 正割,TD,38 µm,吹塑薄膜 1% secant, TD, 38 µ m, blow molded film |
520 | MPa | ASTM D882 |
1% 正割,MD,38 µm,吹塑薄膜 1% secant, MD, 38 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
|||
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
MPa | ASTM D882 | |
TD,屈服,38 µm,吹塑薄膜 TD, yield, 38 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
MPa | ASTM D882 | |
MD,屈服,38 µm,吹塑薄膜 MD, yield, 38 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
38 µm,吹塑薄膜 38 µ m, blow molded film |
g | ASTM D1709-A | |
撕裂强度 tear strength |
|||
MD,38 µm,吹塑薄膜 MD, 38 µ m, blow molded film |
g | ASTM D1922 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
TD,38 µm,吹塑薄膜 TD, 38 µ m, blow molded film |
g | ASTM D1922 | |
氧传输速率 Oxygen transfer rate 2 |
|||
23℃,38 µm,吹塑薄膜 23 ℃, 38 µ m, blow molded film 2 |
cm³/m²/24 hr | ASTM D1434 | |
水气透过率 Water vapor transmittance |
|||
38℃,100% RH,38 µm,吹塑薄膜 38 ℃, 100% RH, 38 µ m, blow molded film |
g/m²/24 hr | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
低摩擦穿刺 Low friction puncture |
|||
吹塑薄膜,38.0 µm Blow molded film, 38.0 µ m |
J/cm | Internal Method |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0% RH |
【新闻资讯】查看全部
安利股份成为耐克鞋用聚氨酯合成革供应商
2021-03-22 搜料网资讯: 近日, 安利股份通过美国耐克公司(NIKE,Inc.)全球鞋用材料认证,成为耐克公司唯一中资鞋用 聚氨酯 合成革和复合材料合格供应商,安利材料将扮靓耐克产品。 安利股份 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |