| 牌号简介 About |
|---|
| IROGRAN® A 60 E 4902是一种柔软、高性能聚酯基热塑性聚氨酯,用于挤压和成型应用。Irograna 60 E 4902是亨斯迈薄膜和片材以及注塑产品系列的一部分。它可在低温下加工,并提供一种特别设计的、灵活的材料,适用于弹性薄膜和模件。性能特点优良的弹性、优异的磨损性能、良好的低温弹性、增强的水解稳定性、增强的紫外线稳定性、低温加工性 IROGRAN A 60 E 4902 is a soft, high performance polyester based thermoplastic polyurethane intended for extrusion and moulding applications. IROGRANA 60 E 4902 is part of the HUNTSMAN Film and Sheet and Injection-Moulding product ranges. It is processable at low temperatures and offers a specially designed, flexible material suitable for elastic films & mouldings. PERFORMANCE FEATURES Excellent elasticity Excellent wear performance Good low temperature flexibility Enhanced Hydrolytic Stability Enhanced UV stability Low temperature processability |
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density 2 |
1.14 | g/cm³ | ASTM D792 |
|
密度 Density 3 |
1.14 | g/cm³ | DIN 53478 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
160℃,8.7 kg 160℃,8.7 kg |
35.0 | cm³/10min | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
注册或登录后
所有资料免费
|
DIN 53505 | |
|
邵氏 A,注塑成型 Shaw A, injection molding |
注册或登录后
所有资料免费
|
DIN 53505 | |
|
邵氏 D,注塑成型 Shaw's D, injection molding |
注册或登录后
所有资料免费
|
DIN 53505 | |
|
邵氏硬度 Shore hardness |
注册或登录后
所有资料免费
|
ASTM D2240 | |
|
邵氏 A,注塑成型 Shaw A, injection molding |
注册或登录后
所有资料免费
|
ASTM D2240 | |
|
邵氏 D,注塑成型 Shaw's D, injection molding |
注册或登录后
所有资料免费
|
ASTM D2240 | |
|
磨耗量 Wear amount 2 |
注册或登录后
所有资料免费
|
||
|
-- -- |
注册或登录后
所有资料免费
|
mm³ | DIN 53516 |
|
-- -- |
注册或登录后
所有资料免费
|
mm³ | ASTM D395 |
|
弹性体 Elastomer |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Tensile Set(200% Strain) Tensile Set(200% Strain) 3 |
注册或登录后
所有资料免费
|
% | ASTM D412 |
|
Tensile Set(200% Strain) Tensile Set(200% Strain) 3 |
注册或登录后
所有资料免费
|
% | DIN 53504 |
|
拉伸强度 tensile strength 4 |
注册或登录后
所有资料免费
|
||
|
断裂,0.635 mm Fracture, 0.635 mm 4 |
注册或登录后
所有资料免费
|
MPa | ASTM D412 |
|
断裂,0.635 mm Fracture, 0.635 mm 4 |
注册或登录后
所有资料免费
|
MPa | DIN 53504 |
|
300% 应变,0.635 mm 300% strain, 0.635 mm 4 |
注册或登录后
所有资料免费
|
MPa | DIN 53504 |
|
300% 应变,0.635 mm 300% strain, 0.635 mm 4 |
注册或登录后
所有资料免费
|
MPa | ASTM D412 |
|
100% 应变,0.635 mm 100% strain, 0.635 mm 4 |
注册或登录后
所有资料免费
|
MPa | DIN 53504 |
|
100% 应变,0.635 mm 100% strain, 0.635 mm 4 |
注册或登录后
所有资料免费
|
MPa | ASTM D412 |
|
拉伸应变 Tensile strain 4 |
注册或登录后
所有资料免费
|
||
|
断裂,0.635 mm Fracture, 0.635 mm 4 |
注册或登录后
所有资料免费
|
% | DIN 53504 |
|
断裂,0.635 mm Fracture, 0.635 mm 4 |
注册或登录后
所有资料免费
|
% | ASTM D412 |
|
撕裂强度 tear strength 4 |
注册或登录后
所有资料免费
|
||
|
0.635 mm 0.635 mm 4 |
注册或登录后
所有资料免费
|
kN/m | DIN 53515 |
|
0.635 mm 0.635 mm 4 |
注册或登录后
所有资料免费
|
kN/m | ASTM D624 |
|
压缩形变 Compression deformation 2 |
注册或登录后
所有资料免费
|
ASTM D395 | |
|
23℃,70 hr 23℃,70 hr |
注册或登录后
所有资料免费
|
% | ASTM D395 |
|
70℃,24 hr 70℃,24 hr |
注册或登录后
所有资料免费
|
% | ASTM D395 |
|
压缩形变 Compression deformation 2 |
注册或登录后
所有资料免费
|
DIN 53517 | |
|
23℃,70 hr 23℃,70 hr |
注册或登录后
所有资料免费
|
% | DIN 53517 |
|
70℃,24 hr 70℃,24 hr |
注册或登录后
所有资料免费
|
% | DIN 53517 |
|
巴肖氏弹性 Basho's elasticity |
注册或登录后
所有资料免费
|
% | ASTM D2632 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
熔融温度 Melting temperature |
注册或登录后
所有资料免费
|
℃ | 内部方法 |
|
TMA TMA 4 |
注册或登录后
所有资料免费
|
Internal Method | |
|
High:635.0 µm High:635.0 µm |
注册或登录后
所有资料免费
|
℃ | Internal Method |
|
Low:635.0 µm Low:635.0 µm |
注册或登录后
所有资料免费
|
℃ | Internal Method |
| 备注 |
|---|
| 1 一般属性:这些不能被视为规格。 |
| 2 Injection Molded |
| 3 Extruded Film, 0.025 in |
| 4 Extruded Film |
|