牌号简介 About |
---|
JAMPLAST高光泽树脂是一种热塑性材料,它提供了各种聚合物成分所赋予的加工性、耐冲击性和耐热性的极好平衡。JAMPLAST ABS树脂可用于各种不同的熔体流动速率、冲击强度和耐热性,适用于通过注塑、片材或型材挤压和热成型工艺制造的高光泽和低光泽应用。JAMPLAST ABS树脂旨在提供广泛的冲击强度和熔体流动速率,以满足耐用品注射成型市场的需求。本产品的典型Izod冲击强度值为4至7.5 ft-lb/in,熔化流速为2.5至7.0 g/10 min。对于最高光泽树脂,光泽值通常大于60°Gardner标度的95%,对于光泽范围更广的产品,光泽值大于90%。JAMPLAST ABS树脂提供更广泛的光泽范围,同时保持中等的冲击强度和中等的熔体流动速率。 Jamplast high gloss resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. Jamplast ABS resins are available in a wide range of melt flow rates, impact strength and heat resistance for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion and thermoforming processes. Jamplast ABS resins are designed to offer a wide range of impact strengths and melt flow rates to meet the needs of the durables injection molding markets. This product offers typical Izod impact strength values from 4 to 7.5 ft-lb/in and melt flow rates ranging from 2.5 to 7.0 g/10 min. The gloss values are typically greater than 95% on the 60° Gardner scale for the highest gloss resins and greater than 90% for those products having a broader range of gloss. Jamplast ABS resin offers a broader range of gloss while maintaining medium impact strength with a medium melt flow rate. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.40 到 0.70 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 1 |
2240 | MPa | ASTM D638 |
拉伸强度 tensile strength 1 |
ASTM D638 | ||
屈服 yield |
44.8 | MPa | ASTM D638 |
断裂 fracture |
31.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain 1 |
|||
断裂 fracture 1 |
% | ASTM D638 | |
弯曲模量 Bending modulus 2 |
MPa | ASTM D790 | |
弯曲强度 bending strength 2 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 3 |
ASTM D256 | ||
-18℃,3.2mm -18℃,3.2mm |
J/m | ASTM D256 | |
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 4 |
ASTM D3763 | ||
-18℃,3.18 mm,Peak Energy -18℃,3.18 mm,Peak Energy |
J | ASTM D3763 | |
-18℃,3.18 mm,Total Energy -18℃,3.18 mm,Total Energy |
J | ASTM D3763 | |
23℃,3.18 mm,Peak Energy 23℃,3.18 mm,Peak Energy |
J | ASTM D3763 | |
23℃,3.18 mm,Total Energy 23℃,3.18 mm,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
UL 94 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60° 60° |
ASTM D523 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1, 2,0 in/min |
3 类型 1, 0,050 in/min |
4 10 mil 缺口深度 |
5 11,1 ft/sec |
【新闻资讯】查看全部
再生碳纤维3D打印,运用于新一代列车
2018-06-07 碳纤维是一种现代高性能材料,被广泛应用于要求部件具有机械强度但又十分轻质的领域中,例如航空航天、汽车行业,以及风能技术和现代体育器材中。但由于其高昂的成本,成为许多制造商的障碍。 由于每年会有成千上万吨碳 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |